1) hot corrosion
热腐蚀，高温腐蚀
2) high-temperature corrosion
高温腐蚀
1.
Investigations on outer thermal spraying and inner shot blasting on boiler tube to promote high-temperature corrosion resistance;
采用外壁喷涂与内壁喷丸方法提高锅炉高温受热面管抗高温腐蚀性能的试验
2.
The large amount of vanadium in Orimulsion may cause unexpected problems in the prevention of high-temperature corrosion of furnace.
奥里油中含钒量较多,是锅炉预防高温腐蚀设计中的大难题。
3.
The mechanism of high-temperature corrosion on water-wall of coal-fired boilers in thermal power plants has been briefly presented, and preventive countermeasures being put forward directing against different causes of high-temperature corrosion, the prevention technology of spraying corrosion-resistant metallic coatings onto surface of the water-wall being emphatically narrated.
简要介绍了火电厂燃煤锅炉水冷壁高温腐蚀机理,并针对不同的高温腐蚀原因提出了防护对策。
3) high temperature corrosion
高温腐蚀
1.
Study on high temperature corrosion resistance of FeCrAl and NiCr alloy coating;
FeCrAl和高镍铬合金涂层的抗高温腐蚀性能研究
2.
High Temperature Corrosion of Superheater Tube Materials in Pulverized Coal-Fired Environment;
粉煤燃烧环境中过热器管材的高温腐蚀
3.
Cause analysis of high temperature corrosion and precautionary measures for a 300MW boiler furnace;
燃煤锅炉炉膛高温腐蚀原因及对策
4) corrosion at high temperature
高温腐蚀
1.
This paper represents the mechanism of the water wall tube corrosion at high temperature and the principle of spraying Ni-Cr alloy anticorrosion coat , and introduces the characteristics of the high speed arc spraying and construction technology , at the same time also introduces the method of coat quality inspection.
初步阐述了水冷壁管高温腐蚀的机理及喷涂Ni-Cr合金防腐涂层的原理,介绍了高速电弧喷涂技术的特点、施工工艺,同时也介绍了涂层质量的检测方法。
5) High heat
高热腐蚀
6) low temperature hot corrosion
低温热腐蚀
1.
The results indicate thatlow temperature hot corrosion of the alloy occurs at 550℃ and develops as pitting attack resulted fromsulfidation mechanism.
由于合金表面生成CoO并在表面形成熔融态硫酸盐而逐渐进入加速腐蚀阶段,使合金遭受严重的低温热腐蚀。
补充资料：热腐蚀
分子式：
CAS号：
性质：高温腐蚀的一种类型，待指金属材料在高温环境中由于表面覆盖一薄层液态电解质而发生的加速腐蚀现象。主要发生在燃汽轮机和石油化工燃烧炉等装置中，燃料中的硫与其他杂质在高温下反应生成以硫酸钠为主的低熔点混合物，以熔融状态附着在高温金属部件表面，导致复杂的硫化-氧化反应，使腐蚀加剧。
CAS号：
性质：高温腐蚀的一种类型，待指金属材料在高温环境中由于表面覆盖一薄层液态电解质而发生的加速腐蚀现象。主要发生在燃汽轮机和石油化工燃烧炉等装置中，燃料中的硫与其他杂质在高温下反应生成以硫酸钠为主的低熔点混合物，以熔融状态附着在高温金属部件表面，导致复杂的硫化-氧化反应，使腐蚀加剧。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条