1) sulphide corrosion
硫化腐蚀
1.
The results showed that the tubes had suffered the high temperature oxidative and sulphide corrosion for the operation temperature being higher than the suitable, though reheating tubes were made by Cr5Mo steel which has good anticorrosion and mechanism performance.
应用扫描电子显微镜、能谱分析以及X射线衍射仪对焦化加热炉炉管的高温腐蚀形貌,腐蚀物成分以及物相进行了分析,结果表明,尽管加热炉管用材是抗腐蚀性能和高温机械性能均良好的Cr5Mo钢,但由于炉膛操作温度过高,且燃料中含硫,炉管不但发生高温氧化腐蚀,还发生硫化腐蚀,使破坏加速,最终导致炉管失效。
2) sulfur corrosion
硫化腐蚀
1.
The wear resistant of the welding composites was three times better than that of steel 45, and the sulfur corrosion resistant ability was one time better than that of heat resistant steel 1Cr25Ni20 and increased 50% than that of Co base alloy Stellite 6.
用粉末冶金法制备WC/Ni3 Al复合材料焊条 ,堆焊于 1Cr2 5Ni2 0耐热钢的表面 ,获得的复合材料的耐磨粒磨损性能是4 5钢的 3倍以上 ,耐硫化腐蚀性高于 1Cr2 5Ni2 0耐热钢 1倍 ,高于钴基合金Stellite 6约 5 0 %。
3) H_2S Corrosion
硫化氢腐蚀
1.
The principle of H_2S corrosion is analyzed.
分析了硫化氢腐蚀钢材的原理,针对耐硫化氢腐蚀环境,就合金元素及微合金化、控制轧制对低合金高强度钢组织及性能的影响进行论述,提出了耐硫化氢腐蚀的低合金高强度钢的设计思路。
4) hydrogen sulfide corrosion
硫化氢腐蚀
1.
Hydrogen Sulfide Corrosion Study of Water Injection Wellbore;
注水井井筒硫化氢腐蚀研究
5) H2S corrosion
硫化氢腐蚀
1.
The H2S corrosion mechanism was analyzed in this paper.
我国存在大量含硫油气田,钻井过程中硫化氢腐蚀与防腐蚀问题一直是一个重要的研究课题。
6) Sulfide corrosion
硫化矿腐蚀
补充资料：有机硫化物腐蚀
分子式：
CAS号：
性质：高温腐蚀的一种类型。主要发生在原油蒸馏和裂解装置中。原油或其他物质中含有的有机硫化物，如硫醇、硫醚、噻吩、多硫化物等，在高温下分解形成硫化氢，腐蚀碳钢和低合金钢制设备管道、管件等。温度在400～450℃之间时腐蚀最为严重，提高钢中的含铬量可显著改善其抗有机硫化物腐蚀的能力。
CAS号：
性质：高温腐蚀的一种类型。主要发生在原油蒸馏和裂解装置中。原油或其他物质中含有的有机硫化物，如硫醇、硫醚、噻吩、多硫化物等，在高温下分解形成硫化氢，腐蚀碳钢和低合金钢制设备管道、管件等。温度在400～450℃之间时腐蚀最为严重，提高钢中的含铬量可显著改善其抗有机硫化物腐蚀的能力。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。