1) high-temperature oxidation corrosion
高温氧化腐蚀
1.
It was confirmed that the failure was caused by the combination effect of high-temperature steam erosion and high-temperature oxidation corrosion.
对取自蒸汽过热炉辐射室集气管出口管线管帽失效部位的材料进行了腐蚀部位宏观形貌检查、化学成分、夹杂物、金相组织、氧化物、扫描电镜观察及能谱分析,认为封头是在高温蒸汽的冲刷腐蚀和高温氧化腐蚀的联合作用下破坏的。
3) high-temperature oxidation and corrosion
高温氧化及腐蚀
4) high temperature sulphidization corrosion
高温硫化腐蚀
5) corrosion by high temperature H 2S
高温硫化氢腐蚀
6) high-temperature corrosion
高温腐蚀
1.
Investigations on outer thermal spraying and inner shot blasting on boiler tube to promote high-temperature corrosion resistance;
采用外壁喷涂与内壁喷丸方法提高锅炉高温受热面管抗高温腐蚀性能的试验
2.
The large amount of vanadium in Orimulsion may cause unexpected problems in the prevention of high-temperature corrosion of furnace.
奥里油中含钒量较多,是锅炉预防高温腐蚀设计中的大难题。
3.
The mechanism of high-temperature corrosion on water-wall of coal-fired boilers in thermal power plants has been briefly presented, and preventive countermeasures being put forward directing against different causes of high-temperature corrosion, the prevention technology of spraying corrosion-resistant metallic coatings onto surface of the water-wall being emphatically narrated.
简要介绍了火电厂燃煤锅炉水冷壁高温腐蚀机理,并针对不同的高温腐蚀原因提出了防护对策。