织构体,Diamond texture,在线英语词典,英文翻译,专业英语

1) Diamond texture

织构体

2) texture volume fraction

织构体积分数

The relationship between the texture volume fractions and rolling true strain can be quantified by the Avrami type equations.

采用X射线衍射测量了1100铝合金不同变形量的冷轧织构,建立了织构体积分数和轧制真应变的数学关系式。

3) diamond texture

金刚石织构体

There exists one of diamond textures which is always preferably oriented along the direction cd hd and composed of a large number of nanon sized fibre subgrains.

它们通常共存在一个金刚石织构体中，形成共生晶体。

4) high Tc textured superconductor

高温超导织构体

5) texture Y 1-x Nd x Ba 2Cu 3O 7-δ

织构体Y_（1-x）Nd_xBa_2Cu_3O_（7-δ）

6) texture

织构

Study of the deformation texture in drawn copper single crystal wires;

拉拔单晶铜线材形变织构的研究

Influence of hot-rolled parameters on Fe-3%Si steel strip' texture by TSCR;

TSCR热轧工艺参数对Fe-3%Si钢带织构的影响

Relationship between the texture and the valence electron structure of bcc thin films vapor deposited on polycrystal or amorphous substrate;

气相沉积bcc薄膜时的织构与价电子结构的关系

参考词条

立方织构平面织构轧制织构结构/织构纤维织构有利织构变形织构织构性能织构强度微织构组织织构织构演化织构控制爱和真理

补充资料：变形织构

变形织构
deformation texture

　　类别按变形方式不同，变形织构可分为拉丝织构、挤压织构、锻造织构和轧制织构等;按织构类型可分为丝织构(线织构)、面织构和板织构等，它们分别用(uvw>、{入壳z}及{h走l}(uvw)密勒指数表示。(见织构) 金属的点阵结构不同，其变形织构也不同。feC金属的板织构有铜织构{112}(111)、S一织构{123}<634)、黄铜织构{011}(211)以及戈斯织构{011}<100)等;面织构有{110};丝织构有<111)和<10。)。bcc金属的滑移系多，变形织构较复杂，典型的板织构有{100}(011>、{112}(110)、{111}(ixZ)与{111}(110)等;面织构有凌112}，丝织构有(110)。hep金属典型的板织构有{0001}(1120》;面织构有{0001};丝织构有<1010>和<0001)。以上变形织构各组分的相对强弱受合金元素的性质和含量、晶粒大小和形状、晶界和相界特性、变形热力学条件以及应力应变状态等许多内外因素的影响和控制。如feC金属越纯或轧制温度较高(不发生动态再结晶)时，{212}(212)与{123}(634)组分越强，易形成“铜型”织构，如图1所示;相反，合金元素含量较高或轧制温度低或变形程度大时，{011}(Zn>与{。11}(10山组分强，其他组分弱，易形成“黄铜型”织构，如图2所示。有人认为，织构由“铜型”向“黄铜型”转化受交滑移控制，但越来越多的研究表明，上述织构类型的转化是由孪生变形引起的。 RD叠强度水平最大9.7 0 .5 1 .0 2.0 3.0 5.0 7.0 图1工业纯铜的轧制织构 (轧制温度:室温，。~95%) 变形织构模型许多科学工作者致力于变形织构形成理论的研究，提出了许多塑性变形模型，主要有萨克斯(E.Saehs)模型和泰勒(G.1.Taylor)模型，其他模型基本上是由它们派生出来的。1928年萨克斯假RO圆强度水平最大42 0 .5 1 .02(】3 0 5.()7.0 图2 H70黄铜的轧制织构 (轧制温度:室温;。~95%)定各晶粒的受力状态都等于样品的宏观受力状态，并假定各滑移系上临界分切应力re为常数，当滑移系上的分切应力达到几时，该滑移系启动。若已知外施应力状态内，则滑移系s上的分切应力代~二急内(i，j一i，2，3)。式中ij重复表示求和，m乙一n“，a‘b‘”a，，:‘”为滑移系s滑移平面的法向矢量;b闭为滑移方向矢量;a为应力张量内坐标系矢量;括号内字母重复表示不求和。该模型适用于单晶体的自由变形，按最大取向因子m补选取滑移系s。但该模型对多晶体来说，忽视了各晶粒之间变形的相互限制和协调，各晶粒之间会形成“孔洞”或“堆集”。一些研究者放松了晶体的变形只由最大取向因子选取滑移系的限制，或者规定了对变形体外形的限制。尽管这样，该模型难以描述多晶体的塑性变形。 1938年泰勒提出另一塑性变形模型，假定金属中各晶粒的变形状态与样品的宏观变形状态相同。根据该模型，又考虑体积守恒及d。，一令(m乙十”目’勺。

说明：补充资料仅用于学习参考，请勿用于其它任何用途。

首页 \| 翻译 \| 影视 \| 论坛 \| 索引织构: 织构组分织构演变微观织构液晶织构退火织构

1) Diamond texture 织构体 2) texture volume fraction 织构体积分数 1. The relationship between the texture volume fractions and rolling true strain can be quantified by the Avrami type equations. 采用X射线衍射测量了1100铝合金不同变形量的冷轧织构,建立了织构体积分数和轧制真应变的数学关系式。 3) diamond texture 金刚石织构体 1. There exists one of diamond textures which is always preferably oriented along the direction cd hd and composed of a large number of nanon sized fibre subgrains. 它们通常共存在一个金刚石织构体中，形成共生晶体。 4) high Tc textured superconductor 高温超导织构体 5) texture Y 1-x Nd x Ba 2Cu 3O 7-δ 织构体Y_（1-x）Nd_xBa_2Cu_3O_（7-δ） 6) texture 织构 1. Study of the deformation texture in drawn copper single crystal wires; 拉拔单晶铜线材形变织构的研究 2. Influence of hot-rolled parameters on Fe-3%Si steel strip' texture by TSCR; TSCR热轧工艺参数对Fe-3%Si钢带织构的影响 3. Relationship between the texture and the valence electron structure of bcc thin films vapor deposited on polycrystal or amorphous substrate; 气相沉积bcc薄膜时的织构与价电子结构的关系参考词条立方织构平面织构轧制织构结构/织构纤维织构有利织构变形织构织构性能织构强度微织构组织织构织构演化织构控制爱和真理补充资料：变形织构变形织构 deformation texture 　　类别按变形方式不同，变形织构可分为拉丝织构、挤压织构、锻造织构和轧制织构等;按织构类型可分为丝织构(线织构)、面织构和板织构等，它们分别用(uvw>、{入壳z}及{h走l}(uvw)密勒指数表示。(见织构) 金属的点阵结构不同，其变形织构也不同。feC金属的板织构有铜织构{112}(111)、S一织构{123}<634)、黄铜织构{011}(211)以及戈斯织构{011}<100)等;面织构有{110};丝织构有<111)和<10。)。bcc金属的滑移系多，变形织构较复杂，典型的板织构有{100}(011>、{112}(110)、{111}(ixZ)与{111}(110)等;面织构有凌112}，丝织构有(110)。hep金属典型的板织构有{0001}(1120》;面织构有{0001};丝织构有<1010>和<0001)。以上变形织构各组分的相对强弱受合金元素的性质和含量、晶粒大小和形状、晶界和相界特性、变形热力学条件以及应力应变状态等许多内外因素的影响和控制。如feC金属越纯或轧制温度较高(不发生动态再结晶)时，{212}(212)与{123}(634)组分越强，易形成“铜型”织构，如图1所示;相反，合金元素含量较高或轧制温度低或变形程度大时，{011}(Zn>与{。11}(10山组分强，其他组分弱，易形成“黄铜型”织构，如图2所示。有人认为，织构由“铜型”向“黄铜型”转化受交滑移控制，但越来越多的研究表明，上述织构类型的转化是由孪生变形引起的。 RD叠强度水平最大9.7 0 .5 1 .0 2.0 3.0 5.0 7.0 图1工业纯铜的轧制织构 (轧制温度:室温，。~95%) 变形织构模型许多科学工作者致力于变形织构形成理论的研究，提出了许多塑性变形模型，主要有萨克斯(E.Saehs)模型和泰勒(G.1.Taylor)模型，其他模型基本上是由它们派生出来的。1928年萨克斯假RO圆强度水平最大42 0 .5 1 .02(】3 0 5.()7.0 图2 H70黄铜的轧制织构 (轧制温度:室温;。~95%)定各晶粒的受力状态都等于样品的宏观受力状态，并假定各滑移系上临界分切应力re为常数，当滑移系上的分切应力达到几时，该滑移系启动。若已知外施应力状态内，则滑移系s上的分切应力代~二急内(i，j一i，2，3)。式中ij重复表示求和，m乙一n“，a‘b‘”a，，:‘”为滑移系s滑移平面的法向矢量;b闭为滑移方向矢量;a为应力张量内坐标系矢量;括号内字母重复表示不求和。该模型适用于单晶体的自由变形，按最大取向因子m补选取滑移系s。但该模型对多晶体来说，忽视了各晶粒之间变形的相互限制和协调，各晶粒之间会形成“孔洞”或“堆集”。一些研究者放松了晶体的变形只由最大取向因子选取滑移系的限制，或者规定了对变形体外形的限制。尽管这样，该模型难以描述多晶体的塑性变形。 1938年泰勒提出另一塑性变形模型，假定金属中各晶粒的变形状态与样品的宏观变形状态相同。根据该模型，又考虑体积守恒及d。，一令(m乙十”目’勺。说明：补充资料仅用于学习参考，请勿用于其它任何用途。