1)  brazing temperature
钎焊温度
1.
Electron beam brazing temperature field PID control system;
电子束钎焊温度场PID控制系统
2.
Effect of processing parameters including brazing temperature and holding time on the joint mechanical property was also discussed by optical microscope,SEM and EDS.
研究表明,钎焊温度为900℃,保温时间为5 min时,接头抗剪强度最高,达144 MPa。
3.
The effects of brazing temperature and time on the structure and property of the brazed joint between graphite and TZM alloys with Ti-based filler in vacuum were presented.
研究了钛合金真空钎焊石墨与TZM合金过程中,钎焊温度和时间对钎焊接头组织和性能的影响。
2)  soldering temperature
钎焊温度
1.
The method to ensure proper soldering temperature and the principle for that is also dealt with.
指出了保证钎焊温度的方法及其原理等。
2.
The results showed that the IMC on the joint boundary indicated the difference in its formation and distribution under different soldering temperatures and times, resulting in the variation of the joint shearing strength.
结果表明:在不同的钎焊温度和钎焊时间条件下,接头界面处金属间化合物的形成及分布是不同的,并由此导致了接头抗剪强度的变化。
3.
The results show that the melting properties of the solder alloy are satisfactory,and the soldering temperature and time have much effect on the shearing-strength of the joints.
制备了急冷型SnAgCu系钎料合金,在对其进行熔化特性测定和钎焊工艺试验后,对钎焊接头的力学性能和显微组织进行了测试分析,结果表明:所制备钎料合金的熔化特性满足要求;钎焊温度和钎焊时间对接头的剪切强度有较大影响,工艺参数为275℃×4。
3)  jointing temperature
钎焊温度
1.
As shown from test,with improving of jointing temperature and prolong of heat preservation time,welding seal organize becomes asymmetry and becomes bulky and carrying capacity of welding seal is worst.
试验表明,钎缝组织随着钎焊温度的提高和钎焊保温时间的延长,其成分变得不均匀、组织变得粗大,钎焊接头的承载能力较差。
2.
As shown from test,with improving of jointing temperature and prolong of heat preservation time,welding seal organize becomes asymmetry and becomes crassitude and carrying capacity of welding seal is worst.
试验表明,钎缝组织随着钎焊温度的提高、钎焊保温时间的延长,其成分变得不均匀、组织变得粗大,钎焊接头的承载能力较差。
4)  brazing temperature distribution
钎焊温度场
5)  brazing temperature range
钎焊温度范围
6)  Vacuum brazing temperature
真空钎焊温度