1) CaO-Al2O3-SiO2 system
CaO-Al2O3-SiO2系
1.
Glass transition temperature and glass crystallization temperature of CaO-Al2O3-SiO2 system glass were measured by means of differential thermal analysis(DTA) technique.
利用DTA技术测定了某一配方的CaO-Al2O3-SiO2系玻璃的玻璃转变温度(Tg)与玻璃晶化温度(Tp),在Tg温度稍上,进行了不同温度的预核化处理。
2) CaO-SiO2-Al2O3-MnO system
CaO-SiO2-Al2O3-MnO系
3) FetO-CaO-SiO2-Al2O3 slag system
FetO-CaO-SiO2-Al2O3渣系
4) CaO-SiO2-Al2O3-MgO-FetO slag
CaO-SiO2-Al2O3-MgO-FetO渣系
1.
The phosphorus capacity of CaO-SiO2-Al2O3-MgO-FetO slags was measured by equilibrating the slags in a molybdenum crucible with CO-CO2-Ar gas and Ag-0.
采用气-渣-金平衡法测定CaO-SiO2-Al2O3-MgO-FetO渣系的磷容量,用钼坩埚作为反应容器,Ag-0。
5) CaO-Al2O3-P2O5-SiO2 system
CaO-Al2O3-P2O5-SiO2体系
1.
The water-resistance mechanism of CaO-Al2O3-P2O5-SiO2 system with or without of additional SO4 ions was analyzed by means of XRD and the pore structure analysis.
研究了硫酸根离子对CaO-Al2O3-P2O5-SiO2体系耐水性的影响,通过XRD、SEM及孔结构分析手段对其耐水性机理进行分析。
6) CaO-SiO_2-Al_2O_3-MgO-(CaF_2) slag
CaO-SiO2-MgO-Al2O3(-CaF2)渣系
补充资料：CA
是以精制短棉绒经醋酸活化，在硫酸催化剂存在下，用醋酸和酯酐混合液使之乙酰化，然后加稀醋酸水解到所需的酯化度的产物。按照酯化度不同，可分为一醋酸纤维素、二酯酸纤维素、三醋酸纤维素。酯化度不同而有不同的性质和用途。酯化度大小对溶解性能有很大影响，酯化度降低则在极性溶剂中的溶解度增加，但在非极性溶剂中溶解度减小。醋酸含量60％-61．5％的三醋酸纤维素，因含羟基少，对水不敏感，可溶于二氯甲烷等。醋酸含量51％-58％的二醋酸纤维素为一般工业上用的醋酸纤维素，可溶于丙酮。三醋酸纤维素和
二醋酸纤维素为白色无定形屑状或粉状固体，无明显熔点，220 ℃开始软化。相对密度1．27-1．32，吸水性(24h)1％-4％。
醋酸纤维素可用于配制溶剂型胶粘剂，粘接眼镜、玩具等塑料制品。贮存于阴凉、通风、干燥的库房内。防雨、防晒。
二醋酸纤维素为白色无定形屑状或粉状固体，无明显熔点，220 ℃开始软化。相对密度1．27-1．32，吸水性(24h)1％-4％。
醋酸纤维素可用于配制溶剂型胶粘剂，粘接眼镜、玩具等塑料制品。贮存于阴凉、通风、干燥的库房内。防雨、防晒。