1) CaO-SiO2-MgO-Al2O3-FetO slag system
CaO-SiO2-MgO-Al2O3-FetO渣系
2) CaO-SiO2-Al2O3-MgO-FetO slag
CaO-SiO2-Al2O3-MgO-FetO渣系
1.
The phosphorus capacity of CaO-SiO2-Al2O3-MgO-FetO slags was measured by equilibrating the slags in a molybdenum crucible with CO-CO2-Ar gas and Ag-0.
采用气-渣-金平衡法测定CaO-SiO2-Al2O3-MgO-FetO渣系的磷容量,用钼坩埚作为反应容器,Ag-0。
3) CaO-SiO2-Al2O3-MgO-FetO slags
CaO-SiO2-Al2O3-MgO-FetO五元渣系
1.
The sulphur capacity of CaO-SiO2-Al2O3-MgO-FetO slags with fixed slag composition,at different temperature and under different gas pressure was measured using gas-slag equilibrium techniques.
采用气-渣平衡法,用铂坩埚作反应容器,CO-CO2-SO2-N2混合气体提供体系的氧分压和硫分压,测定了一定炉渣成分,不同温度和气氛条件下CaO-SiO2-Al2O3-MgO-FetO五元渣系的硫容量。
2.
The FetO activities of CaO-SiO2-Al2O3-MgO-FetO slags of fixed component was determined by the solid electrolyte cell: Mo|Mo+MoO2|ZrO2(MgO)|Fe+(FetO)+Ag|Fe under different temperatures and gas ratios.
采用Mo|Mo+MoO2|ZrO2(MgO)|Fe+(FetO)+Ag|Fe固体电解质电池测定不同温度和气氛条件下定组成CaO-SiO2-Al2O3-MgO-FetO五元渣系的FetO活度。
4) FetO-CaO-SiO2-Al2O3 slag system
FetO-CaO-SiO2-Al2O3渣系
5) CaO-SiO_2-Al_2O_3-MgO-(CaF_2) slag
CaO-SiO2-MgO-Al2O3(-CaF2)渣系
6) CaO-Al2O3-SiO2-MgO-CaF2 Pentary Slag Serious
CaO-Al2O3-SiO2-MgO-CaF2五元渣系
补充资料：CA
是以精制短棉绒经醋酸活化，在硫酸催化剂存在下，用醋酸和酯酐混合液使之乙酰化，然后加稀醋酸水解到所需的酯化度的产物。按照酯化度不同，可分为一醋酸纤维素、二酯酸纤维素、三醋酸纤维素。酯化度不同而有不同的性质和用途。酯化度大小对溶解性能有很大影响，酯化度降低则在极性溶剂中的溶解度增加，但在非极性溶剂中溶解度减小。醋酸含量60％-61．5％的三醋酸纤维素，因含羟基少，对水不敏感，可溶于二氯甲烷等。醋酸含量51％-58％的二醋酸纤维素为一般工业上用的醋酸纤维素，可溶于丙酮。三醋酸纤维素和
二醋酸纤维素为白色无定形屑状或粉状固体，无明显熔点，220 ℃开始软化。相对密度1．27-1．32，吸水性(24h)1％-4％。
醋酸纤维素可用于配制溶剂型胶粘剂，粘接眼镜、玩具等塑料制品。贮存于阴凉、通风、干燥的库房内。防雨、防晒。
二醋酸纤维素为白色无定形屑状或粉状固体，无明显熔点，220 ℃开始软化。相对密度1．27-1．32，吸水性(24h)1％-4％。