1) R 2O-CaO-ZnO-Al 2O 3-SiO 2 system
R2O-CaO-ZnO-Al2O3-SiO2系统
2) R2O-RO-Al2O3-B2O3-SiO2 system
R2O-RO-Al2O3-B2O3-SiO2系统
1.
By means of orthodoxy-test and parallel-test, application to Bone-china of R2O-RO-Al2O3-B2O3-SiO2 System has been discussed, through the analysis to mechanism of glaze of R2O-RO-Al2O3-B2O3-SiO2 system and test the capability to fusibility, mucosity, surface tension of R2O-RO-Al2O3-B2O3-SiO2 system.
实验采用正交实验法和对比实验,通过对R2O-RO-Al2O3-B2O3-SiO2系统的成釉机理分析及熔融特性、熔体的粘度和表面张力等性能的测试,探讨了该系统在骨质瓷中的应用。
3) CaO-MgO-Al_2O_3-SiO_2(CMAS) system
CaO-MgO-Al2O3-SiO2系统
4) CaO-Al2O3-SiO2 system
CaO-Al2O3-SiO2系
1.
Glass transition temperature and glass crystallization temperature of CaO-Al2O3-SiO2 system glass were measured by means of differential thermal analysis(DTA) technique.
利用DTA技术测定了某一配方的CaO-Al2O3-SiO2系玻璃的玻璃转变温度(Tg)与玻璃晶化温度(Tp),在Tg温度稍上,进行了不同温度的预核化处理。
5) R_2O-B_2O_3-SiO_2 glassy system
R2O-B2O3-SiO2系统
6) CaO-SiO2-Al2O3-MnO system
CaO-SiO2-Al2O3-MnO系
补充资料：CaO-TiO2-SiO2 ceramics
分子式：
CAS号：
性质：在CaO-TiO2-SiO2三元系统中以CaSiO3与TiO2或以CaTiSiO5与CaTiO3为基料的陶瓷材料。其结构特点是两种晶相共存，性能受晶相比例影响。配比可在一定范围内调节。主要原料为碳酸钙、二氧化钛、二氧化硅，加入少量改性添加剂，经配料、磨细、混合、成型、烧成等工序获得制品，也可先用碳酸钙和二氧化硅高温下合成硅酸钙，用碳酸钙、二氧化硅、二氧化钛高温下合成钛硅酸钙后再进行配料、烧成等，以确保两晶相共存。主要介电性能为：介电常数80～110，介质损耗角正切值(0.8～2.5)×10-4，介电常数温度系数(-450～+550)×10-6/℃。抗电温度(45～55)kV/mm，电阻率(1011～1012)Ω·cm。主要用作温度补偿型陶瓷电容器瓷料。
CAS号：
性质：在CaO-TiO2-SiO2三元系统中以CaSiO3与TiO2或以CaTiSiO5与CaTiO3为基料的陶瓷材料。其结构特点是两种晶相共存，性能受晶相比例影响。配比可在一定范围内调节。主要原料为碳酸钙、二氧化钛、二氧化硅，加入少量改性添加剂，经配料、磨细、混合、成型、烧成等工序获得制品，也可先用碳酸钙和二氧化硅高温下合成硅酸钙，用碳酸钙、二氧化硅、二氧化钛高温下合成钛硅酸钙后再进行配料、烧成等，以确保两晶相共存。主要介电性能为：介电常数80～110，介质损耗角正切值(0.8～2.5)×10-4，介电常数温度系数(-450～+550)×10-6/℃。抗电温度(45～55)kV/mm，电阻率(1011～1012)Ω·cm。主要用作温度补偿型陶瓷电容器瓷料。