您的位置:首页 -> 词典 -> 9Cr2Mo钢冷轧辊
1)  9Cr2Mo steel cold roller
9Cr2Mo钢冷轧辊
2)  9Cr2Mo forged cold-rolled working roll
9Cr2Mo锻钢冷轧工作辊
1.
Analyzing by metallurgical phase and SEM, find out the fracture causation of 9Cr2Mo forged cold-rolled working roll.
通过金相和扫描电镜分析,并配合热处理试验,找出9Cr2Mo锻钢冷轧工作辊断裂失效原因。
3)  cold roller steel
冷轧辊钢
1.
By contrast to hardened 86CrMoV7 cold roller steel,the effects of heat treatment process on the microstructure of new Cr-Ni-Si-Mo-V cold roller steel are studied by means of optical microscopy,transmission electron microscopy and X-ray diffraction,etc.
本文运用光学金相,X射线衍射及透射电子显微分析等手段,并与淬硬86CrMoV7冷轧辊钢进行对比,研究了热处理规范对新型Cr-Ni-Si-Mo-v冷轧辊钢组织的影响。
4)  forged cold roll
锻钢冷轧辊
1.
The trial is done for wearability and resistance to heat shocks of forged cold roll of Cr3, Cr5 series, and the latter shows better in both the properties.
耐磨性和抗热冲击性是锻钢冷轧辊的重要使用性能指标,对邢台机械轧辊(集团)有限公司生产的Cr3系列、Cr5锻钢冷轧辊的耐磨性和抗热冲击性进行了试验研究,结果表明Cr5锻钢冷轧辊比Cr3系列具有更高的耐磨性和抗热冲击性。
5)  9Cr2Mo steel
9Cr2Mo钢
1.
The microstructure and morphology of bainite of 9Cr2Mo steel austenitized at 1 100℃ and isothermally quenched in salt bath at different temperature were studied by metallographic microscope and SEM.
采用光学显微镜和扫描电子显微镜等技术手段观察了经1 100℃奥氏体化的9Cr2Mo钢在不同温度的盐浴中等温淬火后贝氏体的组织形貌。
2.
Different quenching processes with different temperature have first been designed in experiment,and the best quenching process of 9Cr2Mo steel has been gotten under the biggest hardness,meanwhile the quenching processes show that 9Cr2Mo steel can be fully quenched after both water and oil quenching.
实验中首先设计了不同温度的淬火工艺,得出了9Cr2Mo钢得到最大洛氏硬度下的淬火工艺,同时得出9Cr2Mo钢在水和油中都能淬透;再研究不同回火工艺对9Cr2Mo钢洛氏硬度的影响,得出结果:9Cr2Mo钢的洛氏硬度随回火温度的升高先缓慢下降,当回火温度高于300℃时,随着回火温度的升高明显降低。
3.
The anti-abrasion of 9Cr2Mo steel is higher 72% than that of GCr15 steel.
运用JSM-5610LV扫描电镜对德国产X165CrMoV12钢、国产Cr12MoV钢、9Cr2Mo钢、GCr15钢在不同热处理工艺条件下的金相组织、冲击韧性及耐磨性进行了分析。
6)  steel 9Cr2Mo
9Cr2Mo钢
1.
The effect of rare earth elements on thermal shock resistance of cold roller steel 9Cr2Mo was investigated by means of X ray diffraction and metallographic microscopy.
试验结果表明 :稀土元素抑制了热影响区回火时碳化物的析出 ,从而提高了 9Cr2Mo钢抗热冲击性
2.
The effect of rare earth elements on quenching crack resistance of cold roller steel 9Cr2Mo was investigated by means of scanning electron microscope(SEM) and optical microscope.
利用电镜和金相等手段研究了稀土元素对 9Cr2Mo钢抗淬裂性能的影响。
补充资料:[3-(aminosulfonyl)-4-chloro-N-(2.3-dihydro-2-methyl-1H-indol-1-yl)benzamide]
分子式:C16H16ClN3O3S
分子量:365.5
CAS号:26807-65-8

性质:暂无

制备方法:暂无

用途:用于轻、中度原发性高血压。

说明:补充资料仅用于学习参考,请勿用于其它任何用途。
参考词条