2) Friction stir processing
搅拌摩擦加工
1.
Friction stir processing was applied to cast Mg-Nd-Zn-Zr with 3 different parameters.
制定三种参数对Mg-Nd-Zn-Zr稀土镁合金进行搅拌摩擦加工处理(FSP),通过金相实验观察了合金加工前后的显微组织,发现该工艺在很大程度上细化了合金晶粒;通过拉伸实验测量了合金加工前后的常温及170℃高温力学性能,结果发现合金的力学性能较加工前有明显的提高和改善,且有很好的高温性能。
2.
Finally, the recent development of friction stir processing and the applications of FSW are briefly introduced.
从搅拌摩擦焊的工作原理和特点出发,对搅拌摩擦焊工艺参数、焊缝组织及性能进行了评述;最后简要介绍了搅拌摩擦加工的最新发展及在各工业领域中的应用概况。
3.
The results suggest that the friction stir processing at the parameter of 800rpm-100mm/min can cause apparent grain refinement,significant improvement in ductility and ultimate strength,best comprehensive tensile strength of the AZ91 alloy.
采用400rpm-100mm/min,800rpm-100mm/min,800rpm-200mm/min三种工艺参数对铸态AZ91镁合金进行搅拌摩擦加工(FSP)处理,并对合金加工前后的显微组织和拉伸性能及微观断裂机制进行分析。
3) Friction stir process
摩擦搅拌加工
1.
Friction stir processing (FSP) has been applied to fabricate 10 -20 vol.
采用摩擦搅拌加工方法(Friction Stir Process,FSP)制备了-10vol％和-20vol％-ZrO,纳米(-20 nm)颗米粒增强 AZ31镁基复合材料。
4) friction stir
摩擦搅拌
1.
Friction stir surface modification technology can significantly refine the microstructure and eliminate the casting defects of superficial layer based on the dynamic recrystallization resulting from the friction stir heating and the intensively plastic deformation.
摩擦搅拌表面改性技术通过对材料表层进行摩擦加热和机械搅拌,产生强烈塑性变形和动态再结晶,可以显著细化表层组织,消除铸造缺陷。
5) friction stir weld
搅拌摩擦焊
1.
Investigation on defect dynamic echo waveform of friction stir welding;
搅拌摩擦焊焊缝缺陷的超声波动态波形分析
2.
The metal flowing behavior in weld zone has a great influence on the welds mechanical performance in friction stir welding.
搅拌摩擦焊中焊缝材料的流动对焊件性能有很大影响。
3.
The friction stir welding (FSW) of 5 mm thickness plates of 1060 Al/3003 Al was carried out.
搅拌摩擦焊中,材料的流动状态对焊件性能有很大影响。
6) friction stir welding
搅拌摩擦焊
1.
Influences of friction stir welding parameters on microstructure and mechanical properties of dissimilar magnesium alloys joint;
搅拌摩擦焊工艺参数对异种镁合金接头组织和性能的影响
2.
Development and application of friction stir welding;
搅拌摩擦焊接技术的研究进展和应用
3.
Analysis of Defects in Friction Stir Welding of Aluminum Alloy;
铝合金搅拌摩擦焊焊接过程缺陷分析
补充资料：重复
分子式：
CAS号：
性质：指在相同的实验条件下进行反复测定和测量。重复的目的是估计实验误差，提高平均值的测定精度。它是费歇尔(R.A.Fisher)提出的设计试验的三个基本原则之一，其他两个原则是局部控制与随机化。
CAS号：
性质：指在相同的实验条件下进行反复测定和测量。重复的目的是估计实验误差，提高平均值的测定精度。它是费歇尔(R.A.Fisher)提出的设计试验的三个基本原则之一，其他两个原则是局部控制与随机化。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条