1) "point-seed" method
"点籽晶"法
2) point seed
点状籽晶
1.
DKDP crystals were grown by the Z cut point seed (5mm×5mm×3mm) on the basis of the study on the stability of DKDP solution.
本文在研究DKDP溶液稳定性的基础上 ,采用Z切点状籽晶 (5mm× 5mm× 3mm)生长了多块DKDP晶体 ,在2 5 0ml和 10 0 0ml生长瓶中分别获得了在 [10 0 ]和 [0 0 1]向生长速度可达到 3mm/d和 4 5mm/d的点状籽晶生长优质DKDP晶体的生长条件。
3) point-seed rapid growth method
"点籽晶"快速生长法
5) TSSG
顶部籽晶法
1.
A new Nd-activated nonlinear crystal,Na3(La1-xNdx)9O3(BO3)8(Nd:NLBO)with x=3%,was grown by the top-seeded solution growth(TSSG) method.
采用顶部籽晶法生长出掺杂浓度为3%的Nd:Na3La9O3(BO3)8(Nd:NLBO)晶体。
2.
Using top-seeded solution growth(TSSG) method with H3BO3(4N),Li2CO3(4N) and Cs2CO3(4N) as reactants and the mol ratio of Li2CO3:Cs2CO3:H3BO3=1∶1∶11,large CLBO crystal with dimensions of 65 mm×22 mm×12 mm had been grown,and the growth conditions of the CLBO crystal were studied.
以高纯硼酸、碳酸锂和碳酸铯为原料,摩尔比硼酸:碳酸锂:碳酸铯=11∶1∶1,采用顶部籽晶法,生长出尺寸为65 mm×22 mm×12 mm CsLiB6O10(CLBO)单晶,探讨了影响CLBO晶体生长的因素。
6) bottom seeded solution growth
底部籽晶法
1.
A novel crystal growth technique, the bottom seeded solution growth (BSSG), has been developed for crystal growth from high temperature solutions.
为了从高温溶液中生长非一致熔融的单晶材料,发展了一种叫做“底部籽晶法”的新生长方法。
补充资料：铝合金的羽毛状晶
铝合金的羽毛状晶
feathey crystal of aluminium alloy
IUheJ旧deyumooZhuangJ旧g铝合金的羽毛状晶(feathey Crystal of alu-minium anoy)铝合金铸锭中柱状晶的变种，形状类似羽毛的晶粒。是铸锭缺陷的一种。形状近似直线状花边的羽毛状晶亦称为“花边状组织”。羽毛状晶成群出现，每群中羽毛状晶之间近似平行。羽毛状晶是双晶，以(111)晶面为双晶面。铝一镁系合金中的羽毛状晶如图所示。’ 产生羽毛状晶的工艺因素主要是:(1)熔体处于高温平稳状态，有较好的定向结晶条件。(2)在铸造温度下熔体停留时间过长，熔体过热和高度净化，减少结晶前沿形成晶核的数量。(3)合金中加入某些容易产生羽毛状晶的微量元素，如硼和错。 超硬铝合金、工业纯铝和高镁铝合金形成羽毛状晶的几率较大，而高强锻造铝合金2A70(LD7)、防锈铝合金 3A21(LF21)和含镁低于5%的铝镁系合金，基本上不形成羽毛状晶。 铸锭中存在羽毛状晶对其性能影响较大。在塑性加工过程中易在羽毛状晶的双晶面处产生裂纹。制品中残留的未完全破碎的羽毛状晶区会扩大使用性能的各向异性。蘸: 铝一镁系合金铸锭中的羽毛状晶偏光只100 (格长清)