1) the middle-seeded solution growth technique
中部籽晶法
1.
The high-quality BABF crystal with sizes up to 40×30×12 mm3 had been successfully grown by the middle-seeded solution growth technique,and the optical homogeneity of the crystal is △n ≈ 4.
采用新的B2O3-LiF-NaF助熔剂体系,[001]向籽晶,20~40 r/min的转速,1~5℃/d的降温速率,通过中部籽晶法生长出了尺寸为40×30×12 mm3、光学均匀性为△n≈4。
2) TSSG
顶部籽晶法
1.
A new Nd-activated nonlinear crystal,Na3(La1-xNdx)9O3(BO3)8(Nd:NLBO)with x=3%,was grown by the top-seeded solution growth(TSSG) method.
采用顶部籽晶法生长出掺杂浓度为3%的Nd:Na3La9O3(BO3)8(Nd:NLBO)晶体。
2.
Using top-seeded solution growth(TSSG) method with H3BO3(4N),Li2CO3(4N) and Cs2CO3(4N) as reactants and the mol ratio of Li2CO3:Cs2CO3:H3BO3=1∶1∶11,large CLBO crystal with dimensions of 65 mm×22 mm×12 mm had been grown,and the growth conditions of the CLBO crystal were studied.
以高纯硼酸、碳酸锂和碳酸铯为原料,摩尔比硼酸:碳酸锂:碳酸铯=11∶1∶1,采用顶部籽晶法,生长出尺寸为65 mm×22 mm×12 mm CsLiB6O10(CLBO)单晶,探讨了影响CLBO晶体生长的因素。
3) bottom seeded solution growth
底部籽晶法
1.
A novel crystal growth technique, the bottom seeded solution growth (BSSG), has been developed for crystal growth from high temperature solutions.
为了从高温溶液中生长非一致熔融的单晶材料,发展了一种叫做“底部籽晶法”的新生长方法。
4) TSSG method
顶部籽晶提拉法
1.
In this paper,Yb:KY(WO4)2 laser crystal with dimensions of 25 mm×21 mm×18 mm was prepared by TSSG method from the melting agent of K2W2O7.
采用顶部籽晶提拉法(TSSG)从助溶剂K2W2O7中生长出尺寸为25mm×21mm×18mm的Yb:KY(WO4)2激光晶体。
5) top seeded solvent growth
顶部籽晶提拉法
1.
In this paper, high quality Nd~(3+):KGd(WO_4)_2 , Yb~(3+): KGd(WO_4)_2 and Yb~(3+): KY(WO_4)_2 crystal grown by Top Seeded Solvent Growth(TSSG) method were presented.
本文采用顶部籽晶提拉法，以K_2W_2O_7作助溶剂，通过荧光光谱实验选择合适的掺杂浓度，不同温度烧结固相合成晶体原料及助溶剂，设计合理的工艺参数，生长出优质新型激光晶体Nd~(3+)：KGd(WO_4)_2、Yb~(3+)：KGd(WO_4)_2及Yb~(3+)：KY(WO_4)_2。
2.
In this paper, Yb:KYW crystal was grown by Top Seeded Solvent Growth( TSSG) method ,using K_2W_2O_7 as flux, the properties of Yb:KYW crystal were researched based on the study of the choice of the growing method, the raw material pre-processing , the growth technology and the annealing technology .
本文采用顶部籽晶提拉法(TSSG),以K_2W_2O_7为助熔剂,生长出Yb:KYW激光晶体。
6) top-seeded Kyropoulos method
顶部籽晶泡生法
1.
The growth and properties of doping CLBO crystal have been investigated by top-seeded Kyropoulos method.
本文采用顶部籽晶泡生法进行掺杂CLBO晶体的生长及性能研究。
补充资料：多晶莫来石晶须(纤维)
分子式：
CAS号：
性质：莫来石相为主晶相的多晶纤维。化学成分为Al2O3 72％～77％，SiO222％～17％，B2O3 3％～5％，P2O51.5％～3.0％。纤维直径2～7μm，纤维长度20～125μm。使用温度1350℃。多采用溶胶-凝胶法制造。主要用作补强填料，也可作为轻质、隔热保温材料使用。
CAS号：
性质：莫来石相为主晶相的多晶纤维。化学成分为Al2O3 72％～77％，SiO222％～17％，B2O3 3％～5％，P2O51.5％～3.0％。纤维直径2～7μm，纤维长度20～125μm。使用温度1350℃。多采用溶胶-凝胶法制造。主要用作补强填料，也可作为轻质、隔热保温材料使用。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。