1) Ethylene/1-Octene Copolymer
乙烯/辛烯-1共聚物
2) POE
['pəui]
乙烯-1-辛烯共聚物
1.
Application of infrared spectrum in study of graft copolyme POE-g-MAH;
红外光谱在马来酸酐接枝乙烯-1-辛烯共聚物研究中的应用
2.
It prepared glycidyl methacrylate (GMA) grafted ethylene-1-octene (POE) by means of melting method, and characterized its structure by making use of IR spectrum.
采用熔融法制备乙烯-1-辛烯共聚物(POE)接枝甲基丙烯酸环氧丙酯(GMA),利用红外光谱对其结构进行表征。
3.
The maleic anhydride(MAH) was employed as grafting monomer onto polyolefin(elastomer)(POE/PP) by reactive extrusion.
研究了在含有适量聚丙烯的聚烯烃弹性体乙烯-1-辛烯共聚物(POE)熔融接枝马来酸酐(MAH)反应中,引发剂、接枝单体用量、及阻交联剂品种对接枝率的影响及其微观机理。
3) POE
['pəui]
乙烯-辛烯共聚物
1.
The PP–POE–nano CaCO_3 ternary composites were prepared with POE as toughener,nano CaCO_3 as reinforcer.
以乙烯-辛烯共聚物(POE)为增韧剂,以纳米CaCO3为增强剂,将传统弹性体增韧方法与新型纳米粒子增韧增强手段相结合,利用双螺杆挤出机,通过熔融共混工艺制备出了共聚聚丙烯(PP)/POE/纳米CaCO3三元复合材料,研究了纳米CaCO3用量对复合材料的流动性和力学性能的影响,还利用扫描电子显微镜(SEM)对复合材料的断面形态进行了研究。
2.
For obtaining high grafting defree, solvothermal process was developed to graft maleic anhydride (MAH) onto poly(ethylene 1-octene) (POE).
首次尝试用溶剂热合成法制备马来酸酐(MAH)接枝乙烯-辛烯共聚物(POE)共聚物。
3.
POE-g-MAH was prepared by melt grafting.
利用熔融接枝法制备了马来酸酐接枝乙烯-辛烯共聚物(POE-g-MAH),将POE-g-MAH与线型低密度聚乙烯(LLDPE)共混后与铜片进行热复合。
4) ethylene-octene copolymer
乙烯-辛烯共聚物
1.
Flow instability of ethylene-octene copolymer and ethylene-propylene-diene monomer at high speed flow field
乙烯-辛烯共聚物和三元乙丙橡胶在高速流场中的流动不稳定性
2.
Maleic anhydride grafting ethylene-octene copolymer(POE-g-MAH) was prepared by melt grafting.
利用熔融接枝法制备了马来酸酐接枝乙烯-辛烯共聚物(POE-g-MAH),探讨了各个因素对POE-g-MAH接枝率和熔体流动速率(MFR)的影响,并得出了最佳配方、最佳工艺条件。
3.
The effects of viscosity ratio on mechanical properties, morphology, structure and crystallization capacity of blend consisting of polypropylene and ethylene-octene copolymer (PP/POE) were studied.
研究了黏度比对聚丙烯(PP)/乙烯-辛烯共聚物(POE)共混物力学性能、形态结构以及结晶性能的影响。
5) polyethylene-octene elastomer
乙烯-辛烯共聚物
1.
Non-isothermal melt crystallization kinetics of polyethylene-octene elastomer(POE)/starch blends has been investigated by differential scanning calorimeter(DSC).
通过差示扫描量热仪(DSC)研究了乙烯-辛烯共聚物/淀粉共混体系的非等温结晶动力学,用Jeziorny和Ozawa方程描述了结晶动力学过程。
2.
The non-isothermal degradation of polyethylene-octene elastomer(POE)/gelatinized waxy corn starch(GWCS) blends with different compositions was first carried out in an inert atmosphere,and the corresponding degradation behaviors and kinetics were investigated by means of the thermogravimetric(TG) method.
利用动态热重分析(TG)技术对乙烯-辛烯共聚物(POE)/糊化蜡质玉米淀粉(GWCS)共混物在惰性气体条件下的热性能和非等温热解动力学进行了分析,探讨了其热解机理。
6) ethylene/octene copolymer
乙烯/辛烯共聚物
补充资料：乙烯-1-辛烯共聚物
分子式：
CAS号：
性质：是含少量1-辛烯的乙烯共聚物，与乙烯与1-丁烯或1-己烯共聚物相比，性能更柔软、韧性好，黏结强度高，薄膜的拉伸强度和撕裂强度突出，耐穿刺，热封性好。密度0.919g/cm3。熔体指数为lg/10min时的拉伸强度，纵向为45.5MPa，横向为36.7MPa。撕裂伸长率：纵向650％，横向800％。撕裂强度纵向为580g/38μm，横向为840g/38μm。工业生产采用溶液法由乙烯与1-辛烯共聚而成，主要用途是薄膜。
CAS号：
性质：是含少量1-辛烯的乙烯共聚物，与乙烯与1-丁烯或1-己烯共聚物相比，性能更柔软、韧性好，黏结强度高，薄膜的拉伸强度和撕裂强度突出，耐穿刺，热封性好。密度0.919g/cm3。熔体指数为lg/10min时的拉伸强度，纵向为45.5MPa，横向为36.7MPa。撕裂伸长率：纵向650％，横向800％。撕裂强度纵向为580g/38μm，横向为840g/38μm。工业生产采用溶液法由乙烯与1-辛烯共聚而成，主要用途是薄膜。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条