1) POE-g-MAH
马来酸酐接枝乙烯-1-辛烯共聚物
1.
Polyamide 6(PA6)/POE-g-MAH and polyamide 6-clay nanocomposites (NCH)/ POE-g-MAH were prepared with the brittle-tough transition point all at the 8%-10% of POE-g-MAH content in the two blends.
制备了尼龙-6(PA6)/马来酸酐接枝乙烯-1-辛烯共聚物(POE-g-MAH)和PA6-蒙脱土纳米复合物(NCH)/POE-g-MAH两种复合材料,其脆韧转变点都是在POE-g-MAH质量分数为8%～10%。
2) ethylene/octane copolymer grafting maleic anhydride
马来酸酐接枝乙烯辛烯共聚物
3) ethylene-octene copolymer-grafted-maleic
马来酸酐接枝乙烯-辛烯共聚弹性体
1.
Nano CaCO3 and ethylene-octene copolymer-grafted-maleic(M-POE) were used to toughen PET.
采用马来酸酐接枝乙烯-辛烯共聚弹性体(M-POE)和纳米CaCO3协同增韧聚对苯二甲酸乙二酯(PET)。
4) (E/VAC)-g-MAH
马来酸酐接枝(乙烯/乙酸乙烯酯)共聚物
5) ethylene-vinylacetate grafting maleic anhydride copolymer
马来酸酐接枝乙烯醋酸乙烯共聚物
6) maleated ethylene vinyl acetate copolyme
马来酸酐接枝乙烯-醋酸乙烯酯共聚物
1.
The effect of maleated ethylene vinyl acetate copolymer on mechanical properties and flame retardance properties of Mg(OH)-2/EVA nano-composites was studied.
研究了马来酸酐接枝乙烯-醋酸乙烯酯共聚物(MEVA)对氢氧化镁/乙烯-醋酸乙烯酯共聚物纳米复合材料力学性能和阻燃性能的影响。
补充资料：乙烯-1-辛烯共聚物
分子式：
CAS号：
性质：是含少量1-辛烯的乙烯共聚物，与乙烯与1-丁烯或1-己烯共聚物相比，性能更柔软、韧性好，黏结强度高，薄膜的拉伸强度和撕裂强度突出，耐穿刺，热封性好。密度0.919g/cm3。熔体指数为lg/10min时的拉伸强度，纵向为45.5MPa，横向为36.7MPa。撕裂伸长率：纵向650％，横向800％。撕裂强度纵向为580g/38μm，横向为840g/38μm。工业生产采用溶液法由乙烯与1-辛烯共聚而成，主要用途是薄膜。
CAS号：
性质：是含少量1-辛烯的乙烯共聚物，与乙烯与1-丁烯或1-己烯共聚物相比，性能更柔软、韧性好，黏结强度高，薄膜的拉伸强度和撕裂强度突出，耐穿刺，热封性好。密度0.919g/cm3。熔体指数为lg/10min时的拉伸强度，纵向为45.5MPa，横向为36.7MPa。撕裂伸长率：纵向650％，横向800％。撕裂强度纵向为580g/38μm，横向为840g/38μm。工业生产采用溶液法由乙烯与1-辛烯共聚而成，主要用途是薄膜。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。