2) poly(ethylene-propylene-octene)
(乙烯-丙烯-辛烯)共聚物
3) POE
['pəui]
乙烯-1-辛烯共聚物
1.
Application of infrared spectrum in study of graft copolyme POE-g-MAH;
红外光谱在马来酸酐接枝乙烯-1-辛烯共聚物研究中的应用
2.
It prepared glycidyl methacrylate (GMA) grafted ethylene-1-octene (POE) by means of melting method, and characterized its structure by making use of IR spectrum.
采用熔融法制备乙烯-1-辛烯共聚物(POE)接枝甲基丙烯酸环氧丙酯(GMA),利用红外光谱对其结构进行表征。
3.
The maleic anhydride(MAH) was employed as grafting monomer onto polyolefin(elastomer)(POE/PP) by reactive extrusion.
研究了在含有适量聚丙烯的聚烯烃弹性体乙烯-1-辛烯共聚物(POE)熔融接枝马来酸酐(MAH)反应中,引发剂、接枝单体用量、及阻交联剂品种对接枝率的影响及其微观机理。
4) Ethylene/1-Octene Copolymer
乙烯/辛烯-1共聚物
5) propylene-octene-l copolymer
丙烯-辛烯共聚物
6) POE
['pəui]
乙烯-辛烯共聚物
1.
The PP–POE–nano CaCO_3 ternary composites were prepared with POE as toughener,nano CaCO_3 as reinforcer.
以乙烯-辛烯共聚物(POE)为增韧剂,以纳米CaCO3为增强剂,将传统弹性体增韧方法与新型纳米粒子增韧增强手段相结合,利用双螺杆挤出机,通过熔融共混工艺制备出了共聚聚丙烯(PP)/POE/纳米CaCO3三元复合材料,研究了纳米CaCO3用量对复合材料的流动性和力学性能的影响,还利用扫描电子显微镜(SEM)对复合材料的断面形态进行了研究。
2.
For obtaining high grafting defree, solvothermal process was developed to graft maleic anhydride (MAH) onto poly(ethylene 1-octene) (POE).
首次尝试用溶剂热合成法制备马来酸酐(MAH)接枝乙烯-辛烯共聚物(POE)共聚物。
3.
POE-g-MAH was prepared by melt grafting.
利用熔融接枝法制备了马来酸酐接枝乙烯-辛烯共聚物(POE-g-MAH),将POE-g-MAH与线型低密度聚乙烯(LLDPE)共混后与铜片进行热复合。
补充资料：乙烯-1-辛烯共聚物
分子式：
CAS号：
性质：是含少量1-辛烯的乙烯共聚物，与乙烯与1-丁烯或1-己烯共聚物相比，性能更柔软、韧性好，黏结强度高，薄膜的拉伸强度和撕裂强度突出，耐穿刺，热封性好。密度0.919g/cm3。熔体指数为lg/10min时的拉伸强度，纵向为45.5MPa，横向为36.7MPa。撕裂伸长率：纵向650％，横向800％。撕裂强度纵向为580g/38μm，横向为840g/38μm。工业生产采用溶液法由乙烯与1-辛烯共聚而成，主要用途是薄膜。
CAS号：
性质：是含少量1-辛烯的乙烯共聚物，与乙烯与1-丁烯或1-己烯共聚物相比，性能更柔软、韧性好，黏结强度高，薄膜的拉伸强度和撕裂强度突出，耐穿刺，热封性好。密度0.919g/cm3。熔体指数为lg/10min时的拉伸强度，纵向为45.5MPa，横向为36.7MPa。撕裂伸长率：纵向650％，横向800％。撕裂强度纵向为580g/38μm，横向为840g/38μm。工业生产采用溶液法由乙烯与1-辛烯共聚而成，主要用途是薄膜。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条