1) Zirconia fibers
锆氧纤维
2) zirconia fiber
氧化锆纤维
1.
Strengthened with polysulfone (PS) ultra filtration membrane, the tensile strength of the zirconia fiberseparator material was improved from 102g/cm(width) to 198g/cm(width), the alkali absorption was improved from2cm/min to 4cm/min and the other performances, such as the thickness, porosity and surface resistance, were not af-fected.
以聚砜微孔膜为增强体制备增强的氧化锆纤维隔膜材料,可使布膜的强度由原来的102g/cm(宽)提高到现在的198g/cm(宽),吸碱速率由原来的2cm/min提高到现在的4cm/min,而其它的性能如厚度、孔隙率及面电阻等基本不受影响,研制的氧化锆纤维碱性电池隔膜材料基本满足工程化应用的要求。
2.
Process and special capability of zirconia fiber prepared by precursor method are introduced in this paper and the phase transition is also expressed.
氧化锆纤维是一种性能优良的特种无机纤维,耐高温、耐腐蚀、抗氧化,具有广泛的应用前景。
3) zirconia cloth
氧化锆纤维布
1.
Strength of zirconia cloth is effected by several factors.
氧化锆纤维布的强度受到多种因素的影响,当氧化锆纤维布的晶相为四方晶相时,其力学性能最佳;优化布的织物结构可以大幅度提高其强度;PSU和S-PSU对氧化锆纤维布起到增强的作用,PSU也导致其吸碱率和吸碱速率下降,而采用S-PSU代替PSU则对吸碱率和吸碱速率下降会有所改善;通过细化氧化锆晶粒尺寸、提高晶体的完整性、保留气孔结构等方法可以获得高强度的氧化锆纤维布。
4) zirconia fiber products
氧化锆纤维制品
5) polycrystalline zirconium dioxide fibre
多晶二氧化锆纤维
6) Zirconfibre
锆石纤维
补充资料：氧化锆纤维
分子式：
CAS号：
性质：高ZrO2含量的高熔点多晶纤维。直径4～6μm，密度5.6～5.9g/cm3。氧化锆含量99.6％。熔点2593℃。强度350～700MPa。模量126～154GPa。高温抗氧性好，导热系数低，化学稳定。制法：(1)挤压法，将氧化锆胶体或粒子靠增稠剂挤压成细丝，再烧结成纤；(2)溶液纺丝：将锆盐溶液纺成凝胶纤维，热处理和煅烧后制成纤维；(3)浸渍法，将黏胶丝或其织物浸泡于锆盐溶液中，再热解和煅烧而得；(4)采用类似氧化铝纤维的制法制取氧化锆纤维。用作耐烧蚀隔热功能复合材料及结构复合材料增强剂、燃料电池部件等。
CAS号：
性质：高ZrO2含量的高熔点多晶纤维。直径4～6μm，密度5.6～5.9g/cm3。氧化锆含量99.6％。熔点2593℃。强度350～700MPa。模量126～154GPa。高温抗氧性好，导热系数低，化学稳定。制法：(1)挤压法，将氧化锆胶体或粒子靠增稠剂挤压成细丝，再烧结成纤；(2)溶液纺丝：将锆盐溶液纺成凝胶纤维，热处理和煅烧后制成纤维；(3)浸渍法，将黏胶丝或其织物浸泡于锆盐溶液中，再热解和煅烧而得；(4)采用类似氧化铝纤维的制法制取氧化锆纤维。用作耐烧蚀隔热功能复合材料及结构复合材料增强剂、燃料电池部件等。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条