1) zirconfibre,zirconiumsilicatefibre;
硅酸锆纤维
2) aluminium silicate fiber containing zirconia
含锆硅酸铝纤维
1.
The fabrication of aluminium silicate fiber containing zirconia strengthening electronic ceramic body composites was carried out .
以电瓷坯料为基体,以含锆硅酸铝纤维为增强体,分别在1240℃、1250℃、1260℃及1270℃下制备了纤维加入量不同的电瓷复合材料。
3) alumina zirconate fiber
锆酸铝纤维
4) silicon carbide fibers containing zirconium
含锆碳化硅纤维
5) aluminum silicate fibers
硅酸铝纤维
1.
Al2O3-SiO2/AZ91D magnesium matrix composites with compacted structure were prepared with aluminum silicate fibers and AZ91D magnesium alloy by squeeze casting method.
采用硅酸铝纤维和镁合金制备出结构紧密的Al2O3-SiO2/AZ91D镁基复合材料。
2.
Specific to difficult for aluminum silicate fibers into paper and intensity of the paper is not high,Through a series of experiments researched on carboxyl methyl cellulose (CMC),modified polyvi- nyl alcohol (PVA),cationic starch are commonly used on adhesive,which effected on aluminum silicon fibers into paper,performance of strength.
针对硅酸铝纤维难成纸且成纸强度不高的问题,本文通过一系列实验研究了羧甲基纤维素(CMC)、改性聚乙烯醇(PVA)、阳离子淀粉(CS)三种常用胶粘剂对硅酸铝纤维成纸、增强性能的影响。
6) aluminum silicate fiber
硅酸铝纤维
1.
The application of boric acid modified phenolic resin in aluminum silicate fiber paper
硼酸改性酚醛树脂在硅酸铝纤维纸中的应用
2.
To solve the low strength problem of silica aerogel,the nanoporous super insulation materials,reinforced with aluminum silicate fiber,were prepared from TEOS through sol-gel process and supercritical drying technology.
为解决SiO2气凝胶质脆的难题,以正硅酸乙酯为硅源,采用溶胶-凝胶法和超临界干燥工艺制备了硅酸铝纤维增强纳米孔超级绝热材料,容重为74～189 kg。
3.
Flexible micro-porous calcium silicate insulation material is composed of porous spherical agglomerates consisting of many tiny needlelike xonotlite crystals and aluminum silicate fiber,most part of which has been formed flexible ceramic fiber paper before formation of the insulation material.
微孔硅酸钙柔性隔热材料由以硬硅钙石针状微小晶体构成的微孔硅酸钙球形颗粒和硅酸铝纤维复合而成,其中大部分硅酸铝纤维首先形成柔软的纸型材料,微孔硅酸钙颗粒和其余硅酸铝纤维沉积其上,填充在硅酸铝纤维之间的大孔隙中。
补充资料：纤维素基体聚硅酸纤维
分子式：
CAS号：
性质：新型的耐高温阻燃有机-无机混杂纤维，在纤维素基体中含有聚硅酸分子链，二氧化硅填充率为30％～33％。具有低密度和高柔软性，纤维截面呈不规则的腰子形，强度1.5～2cN/dtex，伸长率22％～27％，回潮率9％～11％，吸水率50％～60％，极限氧指数26～33。制法是利用纤维素的再生作用和聚硅酸的聚合作用加以合成，并通过改进的黏胶湿纺工艺制得。用作阻燃装饰织物和防护服、热气体等滤材、摩擦材料、绝热材料、催化剂载体和应急部队的贴身衣等。
CAS号：
性质：新型的耐高温阻燃有机-无机混杂纤维，在纤维素基体中含有聚硅酸分子链，二氧化硅填充率为30％～33％。具有低密度和高柔软性，纤维截面呈不规则的腰子形，强度1.5～2cN/dtex，伸长率22％～27％，回潮率9％～11％，吸水率50％～60％，极限氧指数26～33。制法是利用纤维素的再生作用和聚硅酸的聚合作用加以合成，并通过改进的黏胶湿纺工艺制得。用作阻燃装饰织物和防护服、热气体等滤材、摩擦材料、绝热材料、催化剂载体和应急部队的贴身衣等。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条