1) backfin
压折，缺陷
2) break marks
横折缺陷
1.
The break marks is a kind of strip marks that is vertical to rolling direction, occurring at some locations of hot-rolled steel strip during uncoiling.
热轧低碳钢卷开卷后出现横折缺陷是一种常见现象,无论是国内产品还是进口产品都不同程度地出现横折缺陷,给用户带来许多不便和损失。
2.
Based on spike height resulting in break marks,the new technique of eliminating break marks by getting microstructure of quasi-acicular ferrite in hot strip mill was applied.
根据上下屈服点应力差是产生横折的根本原因,采用"控制显微组织形态,降低上下屈服点应力差"来消除热轧带钢横折缺陷。
3) inner fold defects
内折缺陷
1.
The influence of over-heat and draw speed on inner fold defects of seamless steel tube is analyzed in hot test process of 20 steel from point of view of inner solidified organization of CC billet.
从连铸坯内部凝固组织的角度出发,分析了20钢在热试过程中,过热度、拉速对无缝管内折缺陷的影响,并提出了改善内部组织的措施,以减少内折废品的产生。
4) defect deduction
缺陷折减
5) enfold-defect
折叠缺陷
1.
The cause of extrusion enfold-defect at the top of piston is analyzed,which is because of the thin remainder.
对活塞顶部挤压折叠缺陷产生的原因进行了分析,发现折叠缺陷是由于余料太薄引起的缩尾性折叠;分别对增厚坯料法、方形坯料法和两步挤压法进行了分析比较,结果表明采用增加坯料厚度的方法来防止折叠不仅增加了材料的浪费,也会增大后续的机加工量,是不经济的;方形坯料虽说可以有效的避免活塞顶部金属对流情况,但是会在活塞环岸内侧产生折叠;而两步挤压法有效的防止了活塞销顶部金属对流的情况,有效的避免了活塞顶表面折叠的产生。
6) rack,mark
折痕(压延玻璃缺陷)