1) spelter pot
锌熔液槽
2) molten zinc
熔融锌液
1.
Corrosion and thermal shock behavior of Al_2O_3 ceramic coating in molten zinc
氧化铝涂层在熔融锌液中的腐蚀及热震行为
3) liquid of zincplating
镀锌槽液
4) Molten zinc/aluminum
熔融锌/铝液
5) molten zinc
熔锌
1.
In order to investigate corrosion mechanism of carbon steel in molten zinc as well as effect of Si and C content in steel on zinc corrosion behavior,both microstructure and phase structure of zinc corrosion layer formed on the steel with different contents of Si and C in molten zinc were analyzed using SEM and EDS.
为了研究熔锌对钢铁的腐蚀机制,以及钢铁中硅、碳含量对锌蚀行为的影响,采用扫描电子显微镜及EDS能谱仪对不同碳、硅含量的钢在熔锌中形成的腐蚀层进行组织形貌观察及相结构分析。
2.
Fe2B is a kind of intermetallic compound with perfect behavior on corrosion resistant of molten zinc,but its essential brittleness limits its utility.
金属间化合物Fe_2B除具有金属间化合物的共性外,还具有优良的耐熔锌腐蚀性能,但是它的本质脆性阻碍了它得到进一步的应用。
3.
5B alloy in molten zinc at 600℃ was studied.
5B合金的组织及耐熔锌腐蚀性能的影响。
6) galvanizing bath
镀锌槽、锌浴
补充资料：熔融
分子式：
CAS号：
性质：温度升高时，分子的热运动能增大，导致结晶破坏，物质由晶相变为液相的过程。熔融是一级相转变，熔融有热焓、熵和体积的增大。发生熔融的温度叫熔点或熔融温度。小分子晶体的熔点温度范围很窄（一般小于1℃），而聚合物由于结晶不完全；其熔融温度往往是一个较宽的范围（一般为10～20℃）。
CAS号：
性质：温度升高时，分子的热运动能增大，导致结晶破坏，物质由晶相变为液相的过程。熔融是一级相转变，熔融有热焓、熵和体积的增大。发生熔融的温度叫熔点或熔融温度。小分子晶体的熔点温度范围很窄（一般小于1℃），而聚合物由于结晶不完全；其熔融温度往往是一个较宽的范围（一般为10～20℃）。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条