1) granular cementite
粒状渗碳体
2) cementite particle of micron order
微米级颗粒状渗碳体
3) cementite particle
渗碳体粒子
1.
In order to investigate the effect of cementite particles size on dynamic recrystallization(DRX)of ferrite, two different microstructures consisting of ferrite with similar size and cementite particles with different sizes were adopted by quenching and tempering of a low carbon steel.
利用单向热压缩实验和OM、SEM、EBSD及TEM技术,研究了低碳钢铁素体晶粒尺寸相似、渗碳体粒子尺寸不同的两种原始组织在700℃、0。
2.
The results show that during annealing cold-rolled low-carbon martensite decomposed into ferrite and cementite particles.
通过组织观察和力学性能测试,研究了退火温度、变形量对冷轧低碳马氏体的退火组织及力学性能的影响,并与冷轧70%的纯铁进行比较,结果表明:在退火过程中冷轧低碳马氏体分解为铁素体和渗碳体粒子的复相组织。
4) chain shape cementite
链状渗碳体
5) globular cementite
球状渗碳体
6) netted texture cementite
网状渗碳体
1.
Results show that netted texture cementite and centre martensite were the main cause of the sharp fracture.
分析SWRH82B盘条拉拔过程中出现笔尖状断口的原因,指出网状渗碳体、芯部马氏体是产生笔尖状断口的主要原因,提出改善SWRH82B盘条网状渗碳体、芯部马氏体的方法和措施。
补充资料：渗碳体
即碳化铁Fe3C，一般含碳6.67％，是一种具有极高硬度（BHN600以上）的脆性化合物。呈斜方结构。渗碳体的数量、形态和分布对钢和铸铁的性能影响很大。渗碳体是碳在退火和正火钢中以及白口铸铁中的一般存在形式，也是共析组织珠光体的组成之一(另一为铁素体)。在过共析钢中，则作为自由渗碳体，在珠光体晶界呈网状析出，或以片状在晶内析出。当淬火碳钢的回火温度超过约250℃时,马氏体中的过饱和碳以针状或片状渗碳体的形态析出。渗碳体内经常固溶有其他元素。在碳钢中，一部分铁为锰所置换；在合金钢中为铬、钨、钼等元素所置换，形成合金渗碳体。渗碳体不是稳定的碳化物，在长时间退火后将最终分解出自由碳（石墨）。