1) low-silicon cast iron
低硅铸铁
2) high silicon cast iron
高硅铸铁
1.
Corrosion behavior of high silicon cast iron in several kinds of corrosion conditions;
高硅铸铁在多种环境下的腐蚀行为研究
2.
Influence of Cr on microstructure and properties of high silicon cast iron;
铬对高硅铸铁组织与性能的影响
3) high-silicon cast iron
高硅铸铁
1.
The corrosion in producing the high-concentration nitric acid from the low-concentration by magnesium nitrate process could be effectively controlled if 1Cr18Ni9Ti stainless steel, high-silicon cast iron, aluminum, C4 steel and non-metal materials were selected for the important locations of the equipment.
介绍了浓硝酸生产中的主要腐蚀现象 ,指出采用先进的自动控制的硝酸镁法浓缩稀硝酸生产工艺 ,其重要设备重点部位分别选用 1Cr18Ni9Ti不锈钢、高硅铸铁、铝材和C4钢及非金属材料 ,可取得良好的防腐蚀效
4) chlorine-resistant silicon iron
硅钼铸铁
6) low-Cr cast iron
低铬铸铁
1.
The WC and low-Cr cast iron composite layer samples were prepared by casting-penetrating process to improve the wear resistance of the low-Cr cast iron.
为进一步提高低铬铸铁的耐磨性,利用铸渗工艺采用膏块法制备了WC/低铬铸铁复合铸渗层试样。
2.
VS+Ti+Zn compound inoculant plays a favorable role in improving property process of low-Cr cast iron.
在低铬铸铁改性处理中,VS+Ti+Zn复合孕育剂起着良好的孕育处理作用。
补充资料：高硅铸铁
分子式：
分子量：
CAS号：
性质：含硅约14.5%~18.0%的合金铸铁。在室温下能耐盐酸、硝酸、磷酸、乙酸等酸类的腐蚀。其耐蚀性是由于表面生成二氧化硅的薄膜，因此不耐苛性碱和氢氟酸，对还原性酸如盐酸（在沸点或较高温度）、草酸、甲酸等的耐腐蚀性差。为了提高在盐酸中的耐蚀能力，通常加入3.5%~4%的钼，称硅钼铸铁或抗氯硅铁。主要用于制作各种泵、塔、阀、反应锅、冷却器、储槽、管件和管道等设备。缺点是抗伸和抗弯强度小，脆性大，不能用于高压设备，并应避免撞击。
分子量：
CAS号：
性质：含硅约14.5%~18.0%的合金铸铁。在室温下能耐盐酸、硝酸、磷酸、乙酸等酸类的腐蚀。其耐蚀性是由于表面生成二氧化硅的薄膜，因此不耐苛性碱和氢氟酸，对还原性酸如盐酸（在沸点或较高温度）、草酸、甲酸等的耐腐蚀性差。为了提高在盐酸中的耐蚀能力，通常加入3.5%~4%的钼，称硅钼铸铁或抗氯硅铁。主要用于制作各种泵、塔、阀、反应锅、冷却器、储槽、管件和管道等设备。缺点是抗伸和抗弯强度小，脆性大，不能用于高压设备，并应避免撞击。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。