1) low carbon ferrosilicon
低碳硅铁
3) low silicon and low carbon
低硅低碳
4) low carbon low silicon steel
低碳低硅钢
1.
The main problems of low carbon low silicon steel during the early time in the medium-thin slab caster in the No.
济钢第三炼钢厂利用中薄板连铸机生产低碳低硅钢的初期,主要存在钢水成分控制和可浇性的问题。
5) low carbon and low silicon steel
低碳低硅钢
1.
The porduction process of low carbon and low silicon steel Q195-1 is introduced and factors affecting compositions of the steel and counter measures analyzed and it is pointed out that the key to control the compositions of the steel is to control w(C) content in steel at the end-point within the limit of 0.
介绍了Q195-1低碳低硅钢的生产工艺,分析了影响其成分的因素及控制措施,指出将终点钢水w(C)准确控制在0。
2.
The process route of BOF-CC-high speed rolling for production of H08 steel, the typical low carbon and low silicon steel grade and practical production conditions are introduced.
介绍了低碳低硅钢的典型钢种—H0 8采用转炉、连铸和高线工艺的生产情况及工艺控制。
6) 0.11C-0.6Si-1.5Mn cold rolling TRIP
低碳低硅TRIP
补充资料：超低碳不锈钢
分子式：
CAS号：
性质：含碳量低于0.03％的不锈钢，一般指奥氏体不锈钢。不锈钢中的碳含量降低到0.03％以下，即超低碳化，能有效地避免不锈钢出现贫铬区和防止晶间腐蚀敏感性。碳在铁素体不锈钢中的危害更加严重，当大约从927℃；以上快冷时就会沿晶界析出铬的碳化物，形成晶界贫铬区，而在腐蚀环境中容易发生晶间腐蚀，为了避免晶间腐蚀就要求碳含量必须低于0.01％。采用氩氧脱碳精炼法和真空氧脱碳精炼法，都能生产超低碳不锈钢。
CAS号：
性质：含碳量低于0.03％的不锈钢，一般指奥氏体不锈钢。不锈钢中的碳含量降低到0.03％以下，即超低碳化，能有效地避免不锈钢出现贫铬区和防止晶间腐蚀敏感性。碳在铁素体不锈钢中的危害更加严重，当大约从927℃；以上快冷时就会沿晶界析出铬的碳化物，形成晶界贫铬区，而在腐蚀环境中容易发生晶间腐蚀，为了避免晶间腐蚀就要求碳含量必须低于0.01％。采用氩氧脱碳精炼法和真空氧脱碳精炼法，都能生产超低碳不锈钢。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。