1) low silicon iron
低硅生铁
2) low silicon hot metal
低硅铁水
1.
Practices of blowing of low silicon hot metal were introduced in this paper.
介绍了低硅铁水的吹炼工艺实践。
3) low aluminum ferrosilicon
低铝硅铁
4) low-silicon iron
低硅铁
1.
It can save ferro-silicon and reduce cost to add cheap low-silicon iron in molten steel of oxygen top-blown converter to substitute ferro-silicon alloy in full or part to make deoxidation alloying.
在氧气顶吹转炉钢水中加入廉价的低硅铁全部或部分替代硅铁合金进行脱氧合金化，可以节约硅铁合金，降低炼钢成本。
5) hot metal containing low silicon
低硅铁水
1.
The process of steelmaking with hot metal containing low silicon in Steel-making Plant was introduced.
简介了川威炼钢厂低硅铁水冶炼工艺。
2.
Steelmaking with hot metal containing low silicon in converter is difficult because of short of heat, slow lime melting slag formation, less slag for dephosphorization and slag adhesion on oxygen lance and hood.
针对转炉低硅铁水炼钢成渣困难,渣量少不利于脱磷,容易产生粘枪、粘烟罩等问题,在吹炼过程中加入适量熔剂,枪位稍高于正常含硅铁水炼钢,设计化渣效果好、喷溅少的多孔喷头。
6) low carbon ferrosilicon
低碳硅铁
补充资料：低硅生铁
分子式：
CAS号：
性质：含硅量低于0.45％的生铁。一般作为炼钢用生铁，对于转炉，硅的氧化热是作为炼钢主要热源之一，过低则不能达到最终钢水的精炼温度。但最高也不得超出0.85％。对于平炉或电炉，希望生铁中硅含量越低越好，因为两种炉子都是采用外来热源，只是利用它来调节钢的熔毕含碳量。