1) cavitation erosion
空隙腐蚀
2) gasket corrosion (crevice corrosion)
隙腐蚀 (裂隙腐蚀)
3) crevice corrosion
缝隙腐蚀
1.
A study on crevice corrosion behavior of titanium and 00Cr25Ni22Mo2 stainless steel;
工业纯钛和00Cr25Ni22Mo2不锈钢的缝隙腐蚀
2.
Mechanism Analysis of the Crevice Corrosion of Liquid Chlorine Steel Cylinders and Protection Methods
液氯钢瓶缝隙腐蚀的机理分析及防范措施
3.
Although the crevice corrosion of metals had been extensively studied in the past years,it remained lack of direct experimental information of the micro chemical environments and electrochemical conditions inside the corroding crevice.
根据铜电路板缝腐蚀特征,研制了阵列式Ag/AgCl、IrO2电极,设计缝隙腐蚀模拟装置,在0。
4) creep corrosion
裂隙腐蚀
5) gap corrosion
间隙腐蚀
1.
Corrosion cracking at joint of tube-plate and array-tube is a typical kind of gap corrosion.
管板与列管的连接处发生腐蚀是典型的间隙腐蚀情况,避免产生间隙腐蚀的措施是尽量不造成缝隙结构,合理选择耐蚀材料。
6) crevice corrosion
隙间腐蚀<能>
补充资料：缝隙腐蚀
分子式：
CAS号：
性质：在金属表面与其他物体构成缝隙的区域发生的局部腐蚀。由于缝隙内外的溶液不容易交换，在缝内随着腐蚀过程的进行，金属阳离子水解和阴离子向缝内聚集，导致缝内溶液腐蚀性越来越强。金属表面与其他金属或非金属接触处以及污垢、沉积物、锈层下部都可能构成缝隙，导致缝隙腐蚀的缝隙宽度一般为25～100μm。几乎所有金属材料都会发生缝隙腐蚀，其中具有钝化能力的金属如不锈钢、铝合金等在含有活性阴离子(例如氯离子)的介质中最为敏感。为防止缝隙腐蚀，在设备结构设计上应当尽量避免构成缝隙，并减少介质中活性阴离子的含量。
CAS号：
性质：在金属表面与其他物体构成缝隙的区域发生的局部腐蚀。由于缝隙内外的溶液不容易交换，在缝内随着腐蚀过程的进行，金属阳离子水解和阴离子向缝内聚集，导致缝内溶液腐蚀性越来越强。金属表面与其他金属或非金属接触处以及污垢、沉积物、锈层下部都可能构成缝隙，导致缝隙腐蚀的缝隙宽度一般为25～100μm。几乎所有金属材料都会发生缝隙腐蚀，其中具有钝化能力的金属如不锈钢、铝合金等在含有活性阴离子(例如氯离子)的介质中最为敏感。为防止缝隙腐蚀，在设备结构设计上应当尽量避免构成缝隙，并减少介质中活性阴离子的含量。