1) aerospace corrosion
太空腐蚀
2) cavitation corrosion
空泡腐蚀，空穴腐蚀，空蚀
3) Cavitation Erosion
空穴腐蚀
1.
Cavitation Erosion and Wear Resistance of New CrMnNiN Austenite Stainless Steel;
新型CrMnNiN奥氏体不锈钢的抗空穴腐蚀及磨损性能
4) Cavitation corrosion
空泡腐蚀
1.
Failure analysis of cavitation corrosion perforation in offshore petroleum well drilling pipelines;
海上石油钻井管线空泡腐蚀导致穿孔的失效分析
2.
Optical microscope,scanning electronic microscope and other methods were used to analyzed the main cavitation corrosion characteristics of low-carbon steel which has poor corrosion-resistance to cavitation corrosion.
采用光学显微镜、扫描电镜等方法对抗空泡腐蚀能力较差的普通低碳钢的空泡腐蚀主要特征进行了分析。
3.
Review the recently research of corrosion in flow medium of duplex stainless steel, and focused on erosion corrosion and cavitation corrosion mechanism.
介绍了双相不锈钢在流动介质中的磨损腐蚀和空泡腐蚀的研究状况和它的腐蚀机理,分析了当前在这方面研究的成果和进展,认为需要进一步研究二者的交互作用以及腐蚀过程中化学腐蚀与力学损伤的交互作用。
5) cavitation erosion
空泡腐蚀
1.
In order to lose the damage of cavitation erosion, a series of cavitation erosion resistance materials have been developed, including stainless steel, cobalt base alloy, copper base shape memory alloy.
空泡腐蚀是水泵、水轮机、船用螺旋桨、汽车燃气室和其它水利机械过流部位的一种常见的破坏现象。
6) cavitation erosion
空隙腐蚀
补充资料：空泡腐蚀
分子式：
CAS号：
性质：腐蚀流体与金属构件作高速相对运动，引起流体压力分布不均匀，气泡迅速产生和破灭过程反复进行而导致的局部腐蚀。气泡破灭时产生的压力高达400MPa，破坏金属表面的保护膜或使表面发生塑性变形，从而加速腐蚀。多发生在各种泵、水轮机等高速运动的设备、机械中。可以通过减小介质流速或改进设备结构设计等方法避免空泡形成，从而减轻腐蚀。研究空泡腐蚀的发生和发展过程以及测定材料耐空泡腐蚀能力通常有文丘里型装置、转盘型装置、射流冲击型装置、磁致伸缩型装置和压电晶体型装置等。
CAS号：
性质：腐蚀流体与金属构件作高速相对运动，引起流体压力分布不均匀，气泡迅速产生和破灭过程反复进行而导致的局部腐蚀。气泡破灭时产生的压力高达400MPa，破坏金属表面的保护膜或使表面发生塑性变形，从而加速腐蚀。多发生在各种泵、水轮机等高速运动的设备、机械中。可以通过减小介质流速或改进设备结构设计等方法避免空泡形成，从而减轻腐蚀。研究空泡腐蚀的发生和发展过程以及测定材料耐空泡腐蚀能力通常有文丘里型装置、转盘型装置、射流冲击型装置、磁致伸缩型装置和压电晶体型装置等。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。