1) pulling speed
拉晶速度
2) withdrawal rate
拉晶速率
1.
The effects of withdrawal rate on liquid / solid interface morphology, primary arm spacing,precipitation behaviour of (γ+γ') eutectic and γ'particles as well as microstructure of single crystal Ni-base superalloy have been investigated.
研究了拉晶速率对单晶高温合金凝固界面形态、一次臂间距、（γ＋γ＇）共晶和γ＇相析出行为的影响。
2.
In the present investigation,the influence of withdrawal rate on the microstructure and stress rupture properties of a Ni_3Al-based single crystal superalloy IC6SX were studied.
采用螺旋选晶法制备Ni_3Al基单晶合金IC6SX试棒,研究了不同拉晶速率对凝固组织和高温持久性能的影响。
3) crystallization rate
晶化速度
1.
Influences of the quantity of cationic surfactants on the crystallization rate of zeolite 4A and the length of hydrocarbon chain of cationic surfactants on the crystallization rate and particle size distributions of zeolite 4A were studied.
研究了阳离子表面活性剂加入量对4A沸石晶化速度以及阳离子表面活性剂的碳氢链长对4A沸石晶化速度和粒度的影响。
2.
Influences of NaCl on the crystallization rate and the particle size distribution of zeolite 4A were studied.
研究了添加无机盐氯化钠(NaCl)对4A沸石晶化速度以及粒度的影响。
4) Crystallization rate
结晶速度
1.
The results showed that the crystallization rate of the copolymer could be raised by the addition of the cross-li.
结果表明:交联剂可提高共聚物的结晶速度,不明显影响纤维的结晶规整性;扩链剂则降低共聚物的结晶性能,影响纤维结晶结构的规整性,并且其限制链段运动的作用在拉伸时表现得更明显。
2.
The crystallization rate constant, k, and Avrami index, n, were obtained.
结果表明 ,锑系催化剂所得聚酯的结晶速度总体大于钛系催化剂所得聚酯 ,其中以Sb2 O3催化所得聚酯结晶速度最快 ,而Ti(OC4 H9) 4催化所得聚酯结晶速度最慢。
3.
It was shown in experimental results that the crystallization rates increase with the increase of the polyester content and the molecular weight of polyether.
结果发现，结晶速度Ｋ 随聚酯含量增加而增大，随聚醚分子量的增大而增大，交联剂使结晶速度Ｋ 减少。
5) stretching speed
拉伸速度
1.
Effect about the stretching speed and other parameters to fiber bundle slenderizing processing;
拉伸速度及其他参数变化对束纤维细化过程的影响
2.
The effects of stretching speed change and different speed changing positions on the m value determined were discussed.
探讨了拉伸速度的变化和不同变速位置对m值测试结果的影响。
6) deep drawing speed
拉深速度
1.
8mm were simulated and analyzed by the finite element analysis software under different temperatures,different blank holder forces and different deep drawing speeds.
在不同温度、不同压边力和不同拉深速度下,针对厚度为0。
补充资料：多晶莫来石晶须(纤维)
分子式：
CAS号：
性质：莫来石相为主晶相的多晶纤维。化学成分为Al2O3 72％～77％，SiO222％～17％，B2O3 3％～5％，P2O51.5％～3.0％。纤维直径2～7μm，纤维长度20～125μm。使用温度1350℃。多采用溶胶-凝胶法制造。主要用作补强填料，也可作为轻质、隔热保温材料使用。
CAS号：
性质：莫来石相为主晶相的多晶纤维。化学成分为Al2O3 72％～77％，SiO222％～17％，B2O3 3％～5％，P2O51.5％～3.0％。纤维直径2～7μm，纤维长度20～125μm。使用温度1350℃。多采用溶胶-凝胶法制造。主要用作补强填料，也可作为轻质、隔热保温材料使用。