1) macrocrystalline
粗晶的
2) macrocrystalline
粗晶质，粗晶的
3) coarse grain
粗晶
1.
The relation between coarse grain and rupture of casts was found thro ugh analyzing the formation of coarse grains and tests for eliminating coarse gr ains on ZG32Cr06 cast steel.
通过对ZG32Cr0 6铸钢粗晶成因的分析及消除粗晶的工艺性能试验,探讨了粗晶导致铸件断裂的机理。
2.
The cause of surface coarse grain of aluminium profile is analyzed.
表面粗晶与铸棒晶粒度，挤压温度、挤压比、模具设计制作等因素有关，与铸锭Zn含量无关，避开临界变形量是消除粗晶的主要措施。
3.
The coarse grain cemented carbides demonstrates the special properties and applications,with a serials merits,such as few structural defects,high micro-hardness,low micro-strain.
粗晶硬质合金具有特殊性能和用途,尤其是高温粗晶硬质合金具有结构缺陷少、显微硬度高、微观应变小等一系列优点,因此被广泛应用于矿山工具、冲压模具、石油钻采、硬面材料等领域。
4) coarse crystal
粗晶
5) CGHAZ
粗晶区
1.
Effect of Welding Parameters on Low-temperature Toughness in CGHAZ for X80 Pipeline Steel;
焊接工艺参数对X80管线钢焊接粗晶区低温韧性的影响
2.
Thermal cycle of in-service welding and the microstructure & property of CGHAZ of X70 pipeline steel;
X70钢在役焊接热循环及粗晶区组织性能研究
3.
EFFECT OF COOLING TIME ON CGHAZ TOUGHNESS AND MICROSTRUCTURE OF Ti MICROALLOYED STEEL;
冷却时间对Ti微合金钢焊接粗晶区组织及韧性的影响
6) coarse grain defect
粗晶缺陷
1.
Analyse of coarse grain defect in aluminium alloy die forgings;
铝合金模锻件粗晶缺陷浅析
参考词条
补充资料：铝合金挤压制品的粗晶环
铝合金挤压制品的粗晶环
coarse grain ring of extruded aluminium alloy product
IOheJ一nJ一yo zh1P旧de euJ一nghuon铝合金挤压制品的粗晶环(coarse grain ringof extruded aluminium alloy produet)宇吕合金加工制品缺陷的1种。挤压制品末端周边具有粗大的再结晶晶粒区，单孔模挤压呈环形，多孔模挤压呈月牙形。 粗晶环是采用无润滑正向挤压制品中固有的·种缺陷。沿挤压制品周边形成的粗大晶粒区，降低制品的抗拉强度和屈服强度，提高伸长率。如高强硬铝合金2A12(IY12)淬火自然时效状态棒材的粗晶环区(见图)，与正常区相比.纵向么降低84一92MPa，丙2降低60~64MPa才提高3%一4%。 对粗晶环的形成机理各国有许多研究，早期文献认为由于发生二次再结晶而形成;20世纪70年代以来多数研究结果证明是由于亚晶合并产生的一次再结晶形成。 影响粗晶环的因素较多，低锰的合金形成粗晶环严重，含错的合金可减轻粗晶环。铸锭均匀化退火温度高和挤压温度低，均使粗晶环区深度增加。采用反挤压、润滑挤压和冷挤压工艺可显著减轻粗晶环，甚至完全消除。降低热处理温度和缩短保温时间也可减小粗晶环深度。「肇几 高强硬招合金2八1别{_Y12)挤压棒材淬火自然 时效状态的粗晶环 (咚长清)
说明：补充资料仅用于学习参考，请勿用于其它任何用途。