1) microscopic coarse grain
低倍粗晶
2) low cobalt and gross grain
低钴粗晶
3) macrostructure
[,mækrəu'strʌktʃə]
低倍
1.
According to the macrostructure,decide the reasonable cutting length of the steel.
通过现场跟踪试验,找出了连铸方坯轧制方圆钢产生劈头缺陷的原因,并利用低倍检验确定了合理头尾切除长度,通过现场实践,效果显著,有效解决了连铸方坯轧制方圆钢劈头缺陷问题。
4) macro
[英]['mækrəʊ] [美]['mækro]
低倍
1.
Design tension cup-type and jaw , develop equipment, adopt macro electrical erosion equipment by analyzing the test for tension and macro-etching of larger round and complete tension and acid macro-etching test.
通过对大规格圆钢的拉伸、低倍检验进行分析,设计制作拉力碗及钳口、并对低倍酸洗方法及设备进行了改进,采用低倍电腐蚀设备,顺利、快捷地完成大规格圆钢试样拉伸试验及低倍酸浸检验,保证了检验工作的正常进行。
5) coarse grain
粗晶
1.
The relation between coarse grain and rupture of casts was found thro ugh analyzing the formation of coarse grains and tests for eliminating coarse gr ains on ZG32Cr06 cast steel.
通过对ZG32Cr0 6铸钢粗晶成因的分析及消除粗晶的工艺性能试验,探讨了粗晶导致铸件断裂的机理。
2.
The cause of surface coarse grain of aluminium profile is analyzed.
表面粗晶与铸棒晶粒度，挤压温度、挤压比、模具设计制作等因素有关，与铸锭Zn含量无关，避开临界变形量是消除粗晶的主要措施。
3.
The coarse grain cemented carbides demonstrates the special properties and applications,with a serials merits,such as few structural defects,high micro-hardness,low micro-strain.
粗晶硬质合金具有特殊性能和用途,尤其是高温粗晶硬质合金具有结构缺陷少、显微硬度高、微观应变小等一系列优点,因此被广泛应用于矿山工具、冲压模具、石油钻采、硬面材料等领域。
补充资料：铝合金挤压制品的粗晶环
铝合金挤压制品的粗晶环
coarse grain ring of extruded aluminium alloy product
IOheJ一nJ一yo zh1P旧de euJ一nghuon铝合金挤压制品的粗晶环(coarse grain ringof extruded aluminium alloy produet)宇吕合金加工制品缺陷的1种。挤压制品末端周边具有粗大的再结晶晶粒区，单孔模挤压呈环形，多孔模挤压呈月牙形。 粗晶环是采用无润滑正向挤压制品中固有的·种缺陷。沿挤压制品周边形成的粗大晶粒区，降低制品的抗拉强度和屈服强度，提高伸长率。如高强硬铝合金2A12(IY12)淬火自然时效状态棒材的粗晶环区(见图)，与正常区相比.纵向么降低84一92MPa，丙2降低60~64MPa才提高3%一4%。 对粗晶环的形成机理各国有许多研究，早期文献认为由于发生二次再结晶而形成;20世纪70年代以来多数研究结果证明是由于亚晶合并产生的一次再结晶形成。 影响粗晶环的因素较多，低锰的合金形成粗晶环严重，含错的合金可减轻粗晶环。铸锭均匀化退火温度高和挤压温度低，均使粗晶环区深度增加。采用反挤压、润滑挤压和冷挤压工艺可显著减轻粗晶环，甚至完全消除。降低热处理温度和缩短保温时间也可减小粗晶环深度。「肇几 高强硬招合金2八1别{_Y12)挤压棒材淬火自然 时效状态的粗晶环 (咚长清)