2) Methyl methacrylate, butyl methacrylate, hydroxypropyl methacrylatepolymer
甲基丙烯酸正丁酯、甲基丙烯酸羟丙基酯、甲基丙烯酸甲酯的聚合物
3) poly(n-butyl methacrylate/acrylonitrile) fibre
聚(甲基丙烯酸正丁酯/丙烯腈)纤维
4) poly (butyl acrylate) / poly (butyl methacrylate)
聚丙烯酸丁酯/聚甲基丙烯酸丁酯
5) n Butoxypolyethylene glycol methacrylic acid ester
正丁氧基聚乙二醇甲基丙烯酸酯
1.
n Butoxypolyethylene glycol methacrylic acid ester is prepared and its crosslinking effect on absorbing behaviour of superabsorbent polymer is investigated through inverse suspension polymerization.
合成了正丁氧基聚乙二醇甲基丙烯酸酯交联剂 ,通过反相悬浮聚合考察了其对高吸水性树脂吸水性能的效果 ,探讨了聚乙二醇分子量等交联剂合成条件与用量对吸水性树脂性能的影响 ,发现聚乙二醇相对分子质量为 40 0～ 80 0时高吸水树脂吸水性能较好 ,吸水倍率为 35 0～ 5 0 0g/g ,吸盐水倍率超过 6 0g/g ,加压吸水倍率变化
6) polybutylcyanoacrylate
聚氰基丙烯酸正丁酯
1.
Preparation of gemcitabine polybutylcyanoacrylate nanoparticles;
吉西他滨聚氰基丙烯酸正丁酯纳米粒的制备工艺
2.
Preparation and characterization of amphotericin B-polybutylcyanoacrylate nanoparticles;
携载两性霉素B的聚氰基丙烯酸正丁酯纳米粒的制备及特性评价
3.
Preparation of estradiol-polybutylcyanoacrylate nanoparticles;
雌二醇-聚氰基丙烯酸正丁酯纳米粒的制备
补充资料：聚甲基丙烯酸正丁酯
分子式：
CAS号：
性质：甲基丙烯酸正丁酯的均聚物和共聚物。其本体均聚物常温下是透明的弹性体，相对密度1.05，折射率1.483，软化温度30℃，玻璃化温度20℃，拉伸强度6.9MPa，冲击强度11.5kJ/m2，伸长率230％。具有良好的弹性和较高的黏接性。由本体铸型法或悬浮法制备；也可用乳液或溶液共聚法制备共聚物。适用于作复合安全玻璃的透明中间层材料，也可作食品工业和制药工业用薄膜(无毒性)或工艺美术品涂膜。
CAS号：
性质：甲基丙烯酸正丁酯的均聚物和共聚物。其本体均聚物常温下是透明的弹性体，相对密度1.05，折射率1.483，软化温度30℃，玻璃化温度20℃，拉伸强度6.9MPa，冲击强度11.5kJ/m2，伸长率230％。具有良好的弹性和较高的黏接性。由本体铸型法或悬浮法制备；也可用乳液或溶液共聚法制备共聚物。适用于作复合安全玻璃的透明中间层材料，也可作食品工业和制药工业用薄膜(无毒性)或工艺美术品涂膜。