1) poly(tert-butylmethacrylate)
聚甲基丙烯酸叔丁酯
1.
Core/shell composite microparticles with silica nanoparticle as core and crosslinked poly(tert-butylmethacrylate) as shell were prepared by seed-emulsion polymerization utilizing 3-(trimethoxysilyl)propyl methacrylate(MPS) modified silica particles as seeds,tert-butylmethacrylate as monomer and sodium dodecyl sulfate(SDS) as emulsifier.
以甲基丙烯酸-3-(三甲氧基硅基)丙酯(MPS)修饰的SiO2胶体粒子为种子,甲基丙烯酸叔丁酯(tBMA)为单体、十二烷基硫酸钠(SDS)为乳化剂,采用种子乳液聚合法制备了SiO2/聚甲基丙烯酸叔丁酯的核壳复合微粒。
2.
The aim to synthesize the composite microparticles based on silica as core and crosslinked poly(tert-butylmethacrylate) as shell in this work, is to prepare the inorganic/organic core/shell composite microparticles whose shells are composed of crosslinked poly(methacrylic acid) by transforming poly(tert-butylmethacrylate) into poly(methacrylic acid) by hydrolysis.
本文采用种子乳液聚合法制备内核为二氧化硅、壳层为具有交联结构的聚甲基丙烯酸叔丁酯的核壳复合微粒,目的是想通过水解,使聚甲基丙烯酸叔丁酯转变为聚甲基丙烯酸,最后得到壳层为交联聚甲基丙烯酸的无机/有机核壳复合微粒。
2) Methyl methacrylate-tertiary butyl methacrylate-lauryl methacrylate copolymer
甲基丙烯酸甲酯、甲基丙烯酸叔丁酯、甲基丙烯酸十二烷酯的共聚物
3) poly (tert-butyl methacrylate)-b-poly (N-isopropylacrylamide)
聚甲基丙烯酸叔丁酯-b-聚(N-异丙基丙烯酰胺)
4) tert-butyl-α-methacrylate
α-甲基丙烯酸叔丁酯
5) tert-butyl methacrylate
甲基丙烯酸叔丁酯
1.
In this study,a homopolymer and a series of copolymers of tert-butyl methacrylate(TBMA) with methacrylic acid(MAA) and styrene(St) were synthesized.
本研究合成了甲基丙烯酸叔丁酯(TBMA)的均聚物及其与甲基丙烯酸(MAA)、苯乙烯(St)的共聚物,并与二乙烯基醚(BPA-DEVE)和光生酸剂(PAG)构成光敏成像体系。
2.
Macro-intermediate with Br-end Poly(tert-butyl methacrylate)(PtBMA-Br) was synthesized by Atom Transfer Radical Polymerization(ATRP),with ethyl-2-bromopropionate as initiator,a compound system of CuCl/ N,N,N′,N″,N″-penta-methyldiethylenetri-amine(PMDETA) as catalyst.
以α-溴代丙酸乙酯(EPN-Br)为引发剂,氯化亚铜(CuCl)与N,N,N′,N″,N″-五甲基二亚乙基三胺(PMDETA)组成的混合体系为催化剂,使甲基丙烯酸叔丁酯(tBMA)进行原子转移自由基聚合(ATRP),得到了端基为溴原子的聚甲基丙烯酸叔丁酯大分子中间体PtBMA-Br。
3.
The diblock copolymer of styrene and tert-butyl methacrylate was synthesized by anionic polymerization at 10 ℃.
在 10℃下 ,采用阴离子聚合方法合成相对分子质量、嵌段组成均可控且相对分子质量分布窄的苯乙烯 -甲基丙烯酸叔丁酯嵌段共聚物 ,对所得共聚物进行了IR、NMR、TG、TEM等表征 ,表明共聚物为嵌段结
6) tert-butylmethacrylate
甲基丙烯酸叔丁酯
1.
In this paper, a solusion atom transfer radical polymerization (ATRP) of tert-butylmethacrylate (tBMA) was first studied.
本文以α-氯代丙酸乙酯(ECP)为引发剂,2,2′-联二吡啶(bpy)和N,N,N′,N″,N″-五甲基二亚乙基三胺(PMDETA)为配体,氯化亚铜(CuCl)为催化剂,在N,N′-二甲基甲酰胺(DMF)中使甲基丙烯酸叔丁酯(tBMA)进行原子转移自由基聚合(ATRP),考察了不同配体/催化剂条件下tBMA的ATRP反应过程。
2.
Atom transfer radical polymerization(ATRP) of tert-butylmethacrylate(tBMA) was studied using ethyl-2-chloropropionate(ECP) as initiator in DMF.
以α-氯代丙酸乙酯(ECP)为引发剂,N,N,N′,N″,N″-五甲基二亚乙基三胺(PMDE-TA)为配体,在N,N′-二甲基甲酰胺(DMF)溶液中引发甲基丙烯酸叔丁酯(tBMA)进行原子转移自由基聚合(ATRP),调节聚合反应时间得到了端基为氯原子,数均分子量为1。
补充资料：过氧化叔戊酸叔丁酯
分子式：C9H18O3
分子量：174.24
CAS号：927-07-1
性质：无色液体。熔点<-19℃，相对密度（25/25℃）0.854，折光率(nD25)1.410，不溶于水和乙二醇，溶于多数有机溶剂。闪点68-71℃，具有酯的气味。
制备方法：甲酸与异丁醇在硫酸催化下反应生成叔戊酸，再与三氯化磷进行酰氯化反应生成叔戊酰氯。后者与叔丁基过氧化氢在20℃下反应生成过氧化叔戊酸叔丁酯。其中，叔丁基过氧化氢是由双氧水与叔丁醇反应制取的。原料消耗(kg/t)甲酸 1000异丁酸 1250叔丁醇 1400双氧水 9570三氯化磷 820
用途：用作氯乙烯单体悬浮聚合的引发剂，也可用作其他单体游离基聚合的引发剂。
分子量：174.24
CAS号：927-07-1
性质：无色液体。熔点<-19℃，相对密度（25/25℃）0.854，折光率(nD25)1.410，不溶于水和乙二醇，溶于多数有机溶剂。闪点68-71℃，具有酯的气味。
制备方法：甲酸与异丁醇在硫酸催化下反应生成叔戊酸，再与三氯化磷进行酰氯化反应生成叔戊酰氯。后者与叔丁基过氧化氢在20℃下反应生成过氧化叔戊酸叔丁酯。其中，叔丁基过氧化氢是由双氧水与叔丁醇反应制取的。原料消耗(kg/t)甲酸 1000异丁酸 1250叔丁醇 1400双氧水 9570三氯化磷 820
用途：用作氯乙烯单体悬浮聚合的引发剂，也可用作其他单体游离基聚合的引发剂。