1) Ru-B/SiCb
Ni-B/Si_2
2) Ni-B alloy
Ni-B合金
1.
Influence of cerium sulphate on the electroless plating Ni-B alloy were investigated,test shows that depositing rate were increased and corrosion resistance of the coating can be improved with a certain amount of cerium sulphate in the bath.
研究了硫酸铈对化学镀Ni-B合金的影响,通过实验测定得出,镀液中添加一定量的硫酸铈能提高沉积速度和改善Ni-B镀层的耐蚀性能。
2.
The process of electroplating Ni-B alloy on the surface of carbon fiber was investigated.
研究了碳纤维表面电沉积Ni-B合金工艺,结果表明碳纤维的预处理、镀液组分以及电解参数对沉积速度及镀层质量有明显的影响。
3.
TiB_2 powder was coated using Ni-B alloy by electroless plating to improve its spraying performance.
为改善TiB2粉末物性,采用化学镀工艺对其进行包覆Ni-B合金处理。
3) nanometer Ni-B
纳米Ni-B
1.
The study of nanometer Ni-B catalyzing and decomposing hydrazine;
纳米Ni-B对肼的催化分解作用研究
4) Ni-B/SiO_2
Ni-B/SiO2
1.
The supported Ni-B/SiO_2 amorphous catalyst prepared by chemical reduction exhibited high catalytic activity in hydrogenation of acetophenone.
用化学还原法制备Ni-B/SiO2非晶态催化剂,用XRD、SEM等对其非晶态特征进行表征,并用于苯乙酮的催化加氢实验,讨论了加氢反应条件对苯乙酮的转化率及选择性的影响。
5) Ni-Sn-B/SiO 2
Ni-Sn-B/SiO2
6) Ni Ce B
Ni-Ce-B
1.
EXAFS technique was used to quantitatively determine the local structure evolutions of Ni B and Ni Ce B ultrafine amorphous alloys prepared by chemical reduction during the annealed process.
采用同步辐射 EXAFS技术定量地研究化学还原法制备的 Ni-B和 Ni-Ce-B超细非晶态合金中 Ni原子的局域环境结构随退火温度升高而产生的变化 。