1) Co-Ni-B alloy
Co-Ni-B合金
1.
Effect of rare earth lanthanum on deposition rate of electroless Co-Ni-B alloy;
稀土镧对化学镀Co-Ni-B合金沉积速度的影响
2.
The effect of rare earth element cerium on composition and electrochemical characteristics of electroless Co-Ni-B alloy was studied.
研究了稀土元素Ce对化学沉积Co-Ni-B合金成分和电化学行为等的影响,利用等离子光谱仪分析了沉积层的化学组成,在电子天平上测定了合金的沉积速度,使用LK988Ⅱ型电化学分析系统测定了化学沉积过程阴极极化曲线和循环伏安曲线。
2) Ni-Co-B Alloy
Ni-Co-B合金
1.
Electroless Ni-Co-B Alloy Plating on Diamond Surface Under Electromagntic Field;
金刚石表面电磁场下化学镀Ni-Co-B合金研究
3) Co-Ni-B alloy coating
Co-Ni-B合金镀层
1.
The surface of Co-Ni-B alloy coating was composed of ta.
化学镀Co-Ni-B合金镀层表面由圆锥峰构成,较为平整;添加稀土Ce后,镀层变得凹凸不平。
4) Amorphous allys (co-B、 Co-Cu-B、 Co-Ni-B)
非晶态合金(Co-B、Co-Cu-B、Co-Ni-B)
5) Co-Ni-B-La alloy film
Co-Ni-B-La合金镀层
1.
Influences of the mass concentration of La in the bath on the mass fraction of various components and microhardness of Co-Ni-B-La alloy film were studied.
研究了镀液中La的质量浓度对化学沉积Co-Ni-B-La合金镀层各组分质量分数以及合金镀层显微硬度的影响。
6) Ni Co B amorphous alloy
Ni-Co-B非晶态合金
补充资料：Ni3Al基金属间化合物高温合金
Ni3Al基金属间化合物高温合金
Ni_(3)Al-base intermetallic compound superalloy
N一3AIJ一J旧shuJ一an huahewu goowen heJ一nNi3AI基金属间化合物高温合金(Ni3AI一baseintermetallie eompound superalloy)以Ni3AI相为基体的金属间化合物高温合金。Ni3AI作为高温合金材料中的强化相口)早已被人们所熟知。单晶Ni3AI有较好的室温塑性和加工性，但多晶Ni3AI在室温的塑性儿乎为零。1979年，日本和泉修等发现，添加微量硼可使Ni3AI韧化。硼强烈地偏聚于晶界，从而提高晶界的结合强度并使晶界区无序化，因此提高了晶界区塑性变形能力，使Ni3AI的室温拉伸伸长率可达50%以上。纯净N珠AI的室温、高温强度偏低，与高温合金相比需要进一步提高。固溶强化(见高温合金固溶强化)是提高强度的一条有效途径。Ni3AI可以固溶很多元素，其中以错和铅的强化效果最显著。美国橡树岭国家试验室已发展了一系列含铬、错、错等元素的Ni3AI基金属间化合物高温合金，具有良好的强度、塑性和高温抗氧化性。中国也对Ni3AI基合金进行了深入研究，并添加微量镁显著改善了热加工塑性。Ni3AI基合金可能是最先在工业上得到使用的金属间化合物高温合金之一，已制成各种部件在试用，如汽轮机和柴油机的耐热部件、高温模具、加热元件以及航空用的紧固件等。 〔邹敦叙)