1)  BN/AlN
BN/AlN
1.
Adopting the method of spark plasma sintering,we fabricate BN/AlN composites ,which varying the content of BN from 0 to 30wt% .
本文采用先进的放电等离子烧结技术,制备了BN质量分数从0-30%变化的BN/AlN复合材料。
2)  BN-AlN ceramic
BN-AlN复相陶瓷
1.
This thesis mainly consists of three aspects: synthesis of BN ceramic fibers from precursor, preparation of BN powders and hot-pressed BN-AlN ceramic composites.
本文对BN的研究主要包括三个方面：BN粉末的合成；先驱体法合成BN纤维；热压制备BN-AlN复相陶瓷。
3)  BN
BN
1.
Fabrication of Reaction-bonded Si_3N_4-BN Composite;
反应烧结制备Si_3N_4-BN复合材料
2.
Study on the Progress of Fabricating AlN-BN Composite Cramics;
AlN-BN复合陶瓷制备工艺研究进展
3.
Progress in dielectric properties of microwave-transparent AlN-BN composite ceramics;
透微波AlN-BN复合陶瓷介电性能研究进展
4)  turbostratic boron nitride
t-BN
5)  AlN-BN
AlN-BN
1.
Effect of CaF_2 on AlN-BN Ceramic Composites by Hot-pressing;
CaF_2烧结助剂对热压烧结AlN-BN陶瓷复合材料的影响
2.
Hot-pressed AlN-BN Ceramic Composites and Its Dielectric Properties;
热压烧结AlN-BN复合陶瓷的制备及介电性能
3.
Effect of Combined Additives of CaF_2-Y_2O_3 on Microstructrue and Thermal Conductivity of AlN-BN Composite Ceramics;
复合助剂CaF_2-Y_2O_3对AlN-BN复合陶瓷显微结构和热导性能的影响
6)  h-BN
h-BN
1.
Preparation and Characterization of Nickel Clad h-BN Composite Powders and Coating;
Ni/h-BN复合粉末及其涂层的制备与表征
2.
The Synthesis and Performance of New Type h-BN;
新型h-BN的合成及性能研究
参考词条
补充资料：aluminium nitride material AlN
分子式：
CAS号：

性质： 该材料有陶瓷型和薄膜型两种。氮化铝热导率高、绝缘性能好，电阻率高达4×106Ω·cm。热膨胀系数小(2.65～3.80)×10-6K-1，化学性能稳定，在1000℃时才与空气发生氧化。在真空中可稳定到1500℃。致密型氮化铝是抗水的，几乎不与浓无机酸发生反应。密度为3.26g/cm3，熔点2400℃，弹性模量为300～310GPa，抗弯强度为280～350MPa，莫氏硬度为8。A1N陶瓷用粉末冶金法制得。氮化铝薄膜用反应溅射法制得。A1N陶瓷片用于大功率半导体集成电路和大功率的厚膜电路，A1N薄膜用于薄膜器件的介质和耐磨、耐热、散热好的材料表面镀层。

说明：补充资料仅用于学习参考，请勿用于其它任何用途。