2) Slab crack
铸坯裂纹
1.
The reasons of slab crack under unsteady casting were analysed.
分析了非稳态浇注时导致铸坯裂纹产生的原因,通过采取相应的控制措施,降低了非稳态浇注时铸坯裂纹的发生率。
3) Rolled Billet Comer Cracks
轧坯角裂
4) side internal crack of casting billets
铸坯边内裂
5) transverse corner crack
角部横裂
1.
Causes and countermeasures of transverse corner crack on narrow continuous casting slab;
连铸窄板坯角部横裂的成因及对策
6) transverse corner crack
角横裂
1.
This article brings forward the reasons and countermeasures of the transverse corner crack and surface longitudinal crack of the CC slab.
简述了太钢二炼钢厂碳钢连铸生产线生产的板坯出现的缺陷,分析了板坯的角横裂、表面纵裂的成因,提出了防止裂纹而采取的措施。
2.
Longitudinal and transverse corner crack defects were found on the slab surface for peritectic steel grade Q235G cast in Panzhihua Iron and Steel Group Company.
针对攀钢连铸 Q2 35 G等包晶钢生产中出现的铸坯表面裂纹问题 ,在调查分析裂纹特征及其产生原因的基础上 ,发现保护渣传热过强和保护渣流入不均是诱发角横裂产生的主要原因。
3.
The possibility of transverse corner cracking in slab of peritectic carbon steel is greater than that of other carbon steels.
介绍了影响包晶碳钢角横裂的连铸工艺操作和设备。