铝镁复合阻燃剂,aluminum magnesium composite flame retardant,音标,读音,翻译,英文例句,英语词典

您的位置：首页 -> 词典 -> 铝镁复合阻燃剂

1) aluminum magnesium composite flame retardant 点击朗读

铝镁复合阻燃剂

2) complex flame retardant 点击朗读

复合阻燃剂

Application of Al(OH) 3 complex flame retardant in poly (vinyl chloride) cables was introduced.

介绍了氢氧化铝复合阻燃剂在PVC电缆料上的应用效果 ,讨论了阻燃剂含量对材料的阻燃和力学性能的影响。

更多例句>>

3) Compounded fire-retardant 点击朗读

复合阻燃剂

The effect of the compounded fire-retardant composed of superfine Mg(OH) 2 and Br-Sb halogen retardant on HDPE was studied by fire-retardant properties, mechanical properties and SEM analysis.

结果表明,Mg(OH)2 和Br Sb卤素阻燃剂最佳配比为4∶1(质量比)时,综合效果较佳;通过与Mg(OH)2 阻燃剂的对比试验,发现复合阻燃剂能保持复合材料较好的力学性能,而且显著提高了阻燃性能;熔体流动速率(MFR)的测定表明当复合阻燃剂的添加量为40份时,仍能满足加工工艺的要求。

更多例句>>

4) compound flame retardant 点击朗读

复合阻燃剂

Linear low density polyethylene (ethylene propylene diene) copolymer(LLDPE EPDM) composite with good flame retardance was prepared with LLDPE and EPDM as the matrix, surface-treated Mg(OH)_ 2 as the major flame retardant, compound flame retardant of encapsulated red phosphorus and self-made flame retardant S as the flame retardant synergist.

以线性低密度聚乙烯(LLDPE)、(乙烯/丙烯/二烯)共聚物(EPDM)为基体,以经表面处理的氢氧化镁[Mg(OH)2]为主阻燃剂,微胶囊化红磷和自制阻燃剂S为核心的复合阻燃剂为阻燃增效剂,制备了阻燃性能优良的LLDPE/EPDM复合材料。

更多例句>>

5) composite flame retardant 点击朗读

复合阻燃剂

Preparation of Brucite Matrix Composite Flame Retardant; 点击朗读

水镁石基复合阻燃剂制备工艺研究

The flame retarded PP containing this composite flame retardant has low smoke, low toxicity, low density, low cost and good mechanical properties.

采用十溴二苯乙烷与Mg(OH)2及无毒阻燃协效剂等复配,并经偶联剂表面处理复配成低烟、低卤、环境友好的复合阻燃剂。

Flame--retardant PE was prepared by composite flame retardant DBDE/Sb_2O_3 and the effects of DBDE/Sb_2O_3 on the flame retardant properties, mechanical properties and flame retarding theory were discussed.

通过采用新型阻燃剂十溴二苯乙烷(DBDPE)与Sb_2O_3复合对PE进行阻燃改性,研究了DBDE与Sb_2O_3的协同效应,复合阻燃剂对PE阻燃性能、热解性能、物理机械性能的影响。

更多例句>>

6) Composite Fire Retardant 点击朗读

复合阻燃剂

The application of multivariate composite fire retardant in gelatin of fire-resisting glass

多元复合阻燃剂应用于防火玻璃夹层凝胶

更多例句>>

补充资料：用氢氧化镁作阻燃剂制备阻燃PP的方法

聚丙烯（PP）以其密度小、力学性能好、耐化学腐蚀、易加工、耐热变形温度高、价格低廉等突出优点，在许多行业得到了广泛的应用。阻燃PP已成为使用阻燃剂量最大、增长最快的高聚物阻燃材料。氢氧化镁［Mg(OH)2］作为一种无卤阻燃剂，除能阻燃外还有消烟性能，而且脱水温度高，比较适于加工温度较高的PP等高聚物阻燃改性，在降低对环境的危害和材料安全处理方面更能满足有关法规的要求，同时也使阻燃塑料更易于再生利用。特别是Mg(OH)2原料来源丰富，价格低廉，用它作为PP的阻燃剂有较高的经济效益，所以近年全国各地对用Mg(OH)2阻燃PP十分重视。

然而目前多数企业在用Mg(OH)2阻燃PP时，由于Mg(OH)2用量不足，需添加其他阻燃剂，致使配方成本居高不下。为此，笔者谈一下在用Mg(OH)2作PP阻燃剂时应注意的一些事项。用Mg(OH)2阻燃PP时，为使材料达到ＵＬ94Ｖ-０阻燃级（3.2ｍｍ试样），用量应≥60%，不过，如用Mg(OH)2抑烟，则用量可低一些，含40%Mg(OH)2的PP的烟密度仅为未阻燃PP的约1/3。当PP中Mg(OH)2含量达65时，其机械性能，特别是抗冲强度和伸长率均显著劣化。为了使Mg(OH)2阻燃PP材料的力学性能不至下降很多，应选择粒径微细、粒径分布窄而均匀的Mg(OH)2作原料，并进行双偶联表面处理，以改善物料的流变性能，促进混炼加工时通过Mg(OH)2／PP表面导热而避免形成局部热点，并提高Mg(OH)2与PP的相容性，使其能在聚合物中较均匀地分散。

采用这种经处理的Mg(OH)2阻燃PP时，在对PP作增韧改性后，即使高Mg(OH)2含量的阻燃PP也可获得良好的加工性能及物理机械性能。为使Mg(OH)2在PP中均匀分散，可用布斯捏合机（ＢｕｓｓＫｅｎａｄｅｒ），或德国产双螺杆混炼挤出机，或往复式单螺杆混炼挤出机来进行混炼，并采用合理的加料混合混炼方式。例如，可将全部PP及增韧剂与所需量60%的Mg(OH)2第一次加入混合混炼机中先混合混炼数分钟后，再第二次加入余下的Mg(OH)2。

在加料时应注意加料要均匀，计量要准确。若采用密炼机混炼，对Mg(OH)2除采用两次加入法外，还要准确计量装料率在87%～93%范围内较好。当装料率较少时，混炼效果差，当装料率＞95%时，易造成Mg(OH)2凝集结团，难以分散均匀。混炼不均匀不仅使阻燃性能降低，而且拉伸强度和断裂伸长率都降低，制品外观也较差。总之，采用对PP良好的增韧改性，用经特殊表面处理并对粒径及粒度分布控制的Mg(OH)2，采用适宜的混炼机械及两次加料方法，可使Mg(OH)2在PP中分散均匀。这种阻燃PP可兼具很多应用领域所需材料的机械性能及阻燃性能，还具有抑烟、低毒、无卤、不用Ｓｂ2Ｏ３，环境友好，配方成本低的特点，有较高的经济效益和社会效益。

说明：补充资料仅用于学习参考，请勿用于其它任何用途。

参考词条

复合无机阻燃剂 APFRE复合阻燃剂镁铝复合氧化物催化剂复合铝铁钙镁盐絮凝剂阻燃镁合金铝系阻燃剂

镁铝复合镁质阻燃剂磷氮复合阻燃剂低烟阻燃复合剂无卤复合阻燃剂

说明：双击或选中下面任意单词，将显示该词的音标、读音、翻译等；选中中文或多个词，将显示翻译。
	您的位置：首页 -> 词典 -> 铝镁复合阻燃剂 1) aluminum magnesium composite flame retardant 铝镁复合阻燃剂 2) complex flame retardant 复合阻燃剂 1. Application of Al(OH) 3 complex flame retardant in poly (vinyl chloride) cables was introduced. 介绍了氢氧化铝复合阻燃剂在PVC电缆料上的应用效果 ,讨论了阻燃剂含量对材料的阻燃和力学性能的影响。更多例句>> 3) Compounded fire-retardant 复合阻燃剂 1. The effect of the compounded fire-retardant composed of superfine Mg(OH) 2 and Br-Sb halogen retardant on HDPE was studied by fire-retardant properties, mechanical properties and SEM analysis. 结果表明,Mg(OH)2 和Br Sb卤素阻燃剂最佳配比为4∶1(质量比)时,综合效果较佳;通过与Mg(OH)2 阻燃剂的对比试验,发现复合阻燃剂能保持复合材料较好的力学性能,而且显著提高了阻燃性能;熔体流动速率(MFR)的测定表明当复合阻燃剂的添加量为40份时,仍能满足加工工艺的要求。更多例句>> 4) compound flame retardant 复合阻燃剂 1. Linear low density polyethylene (ethylene propylene diene) copolymer(LLDPE EPDM) composite with good flame retardance was prepared with LLDPE and EPDM as the matrix, surface-treated Mg(OH)_ 2 as the major flame retardant, compound flame retardant of encapsulated red phosphorus and self-made flame retardant S as the flame retardant synergist. 以线性低密度聚乙烯(LLDPE)、(乙烯/丙烯/二烯)共聚物(EPDM)为基体,以经表面处理的氢氧化镁[Mg(OH)2]为主阻燃剂,微胶囊化红磷和自制阻燃剂S为核心的复合阻燃剂为阻燃增效剂,制备了阻燃性能优良的LLDPE/EPDM复合材料。更多例句>> 5) composite flame retardant 复合阻燃剂 1. Preparation of Brucite Matrix Composite Flame Retardant; 水镁石基复合阻燃剂制备工艺研究 2. The flame retarded PP containing this composite flame retardant has low smoke, low toxicity, low density, low cost and good mechanical properties. 采用十溴二苯乙烷与Mg(OH)2及无毒阻燃协效剂等复配,并经偶联剂表面处理复配成低烟、低卤、环境友好的复合阻燃剂。 3. Flame--retardant PE was prepared by composite flame retardant DBDE/Sb_2O_3 and the effects of DBDE/Sb_2O_3 on the flame retardant properties, mechanical properties and flame retarding theory were discussed. 通过采用新型阻燃剂十溴二苯乙烷(DBDPE)与Sb_2O_3复合对PE进行阻燃改性,研究了DBDE与Sb_2O_3的协同效应,复合阻燃剂对PE阻燃性能、热解性能、物理机械性能的影响。更多例句>> 6) Composite Fire Retardant 复合阻燃剂 1. The application of multivariate composite fire retardant in gelatin of fire-resisting glass 多元复合阻燃剂应用于防火玻璃夹层凝胶更多例句>> 补充资料：用氢氧化镁作阻燃剂制备阻燃PP的方法聚丙烯（PP）以其密度小、力学性能好、耐化学腐蚀、易加工、耐热变形温度高、价格低廉等突出优点，在许多行业得到了广泛的应用。阻燃PP已成为使用阻燃剂量最大、增长最快的高聚物阻燃材料。氢氧化镁［Mg(OH)2］作为一种无卤阻燃剂，除能阻燃外还有消烟性能，而且脱水温度高，比较适于加工温度较高的PP等高聚物阻燃改性，在降低对环境的危害和材料安全处理方面更能满足有关法规的要求，同时也使阻燃塑料更易于再生利用。特别是Mg(OH)2原料来源丰富，价格低廉，用它作为PP的阻燃剂有较高的经济效益，所以近年全国各地对用Mg(OH)2阻燃PP十分重视。然而目前多数企业在用Mg(OH)2阻燃PP时，由于Mg(OH)2用量不足，需添加其他阻燃剂，致使配方成本居高不下。为此，笔者谈一下在用Mg(OH)2作PP阻燃剂时应注意的一些事项。用Mg(OH)2阻燃PP时，为使材料达到ＵＬ94Ｖ-０阻燃级（3.2ｍｍ试样），用量应≥60%，不过，如用Mg(OH)2抑烟，则用量可低一些，含40%Mg(OH)2的PP的烟密度仅为未阻燃PP的约1/3。当PP中Mg(OH)2含量达65时，其机械性能，特别是抗冲强度和伸长率均显著劣化。为了使Mg(OH)2阻燃PP材料的力学性能不至下降很多，应选择粒径微细、粒径分布窄而均匀的Mg(OH)2作原料，并进行双偶联表面处理，以改善物料的流变性能，促进混炼加工时通过Mg(OH)2／PP表面导热而避免形成局部热点，并提高Mg(OH)2与PP的相容性，使其能在聚合物中较均匀地分散。采用这种经处理的Mg(OH)2阻燃PP时，在对PP作增韧改性后，即使高Mg(OH)2含量的阻燃PP也可获得良好的加工性能及物理机械性能。为使Mg(OH)2在PP中均匀分散，可用布斯捏合机（ＢｕｓｓＫｅｎａｄｅｒ），或德国产双螺杆混炼挤出机，或往复式单螺杆混炼挤出机来进行混炼，并采用合理的加料混合混炼方式。例如，可将全部PP及增韧剂与所需量60%的Mg(OH)2第一次加入混合混炼机中先混合混炼数分钟后，再第二次加入余下的Mg(OH)2。在加料时应注意加料要均匀，计量要准确。若采用密炼机混炼，对Mg(OH)2除采用两次加入法外，还要准确计量装料率在87%～93%范围内较好。当装料率较少时，混炼效果差，当装料率＞95%时，易造成Mg(OH)2凝集结团，难以分散均匀。混炼不均匀不仅使阻燃性能降低，而且拉伸强度和断裂伸长率都降低，制品外观也较差。总之，采用对PP良好的增韧改性，用经特殊表面处理并对粒径及粒度分布控制的Mg(OH)2，采用适宜的混炼机械及两次加料方法，可使Mg(OH)2在PP中分散均匀。这种阻燃PP可兼具很多应用领域所需材料的机械性能及阻燃性能，还具有抑烟、低毒、无卤、不用Ｓｂ2Ｏ３，环境友好，配方成本低的特点，有较高的经济效益和社会效益。说明：补充资料仅用于学习参考，请勿用于其它任何用途。参考词条复合无机阻燃剂 APFRE复合阻燃剂镁铝复合氧化物催化剂复合铝铁钙镁盐絮凝剂阻燃镁合金铝系阻燃剂