1) reactive mechanical grinding
反应球磨法
1.
Mg/C hydrogen storage materials were prepared by reactive mechanical grinding, which is researched in this paper.
本文研究反应球磨法制备镁碳储氢材料,即在镁中添加金属催化剂和经预处理的无烟煤,经充氢球磨制得储氢材料。
2) reaction milling
反应球磨
1.
Preparation of magnesium/carbon nanocomposites for hydrogen storage by reaction milling;
反应球磨法制备镁/碳纳米复合储氢材料
2.
TiC/Cu composite powder were fabricated by reaction milling,which were suppressed and sintered,then TiC dispersionstrengthen Cubased composites materials were fabricated.
采用反应球磨制备Cu/TiC复合粉末,然后进行压制和烧结,制备了TiC弥散强化铜基复合材料;描述了球磨过程中混合粉末的物理化学变化,研究了压制压强与材料致密度和硬度之间的关系。
3.
Dispersion strengthened Al-Al4C3 materials were prepared by using the reaction milling technique.
采用反应球磨技术制备了Al4C3弥散强化铝,其性能由弥散相的含量及制备工艺参数决定,碳含量的最佳范围是2~5%(重量百分比)抗张强度高达620MPa,尤其具有良好的热稳定
3) reaction ball milling
反应球磨
1.
The applications, the studies on the theories and the effect parameters of in are summarized,some important Work on reaction ball milling, especially the SHS during reaction ball milling is introduced.
简述了机械合金化的应用,总结了机械合金化的理论研究及其过程中的影响因素,介绍了近期主要的有关反应球磨的工作,着重叙述了反应球磨中的SHS现象。
2.
The carbon/magnesium hydrogen storage materials were prepared by reaction ball milling under hydrogen atmosphere with Mg and crystallitic carbon which were made from anthracite, sponge coke and activated carbon after carbonization and pre-graphitization and using needle coke, deposited carbon from pyrolysis of acetylene as carbon raw materials.
本文将无烟煤、海绵焦和活性炭经950℃碳化,1500℃预石墨化处理制成微晶碳,以及以针状焦和乙炔热解沉积碳为碳原料,添加到金属Mg中,在氢气气氛下反应球磨制备碳镁储氢材料。
4) solid-liquid reaction milling
反应球磨
1.
The process of Ni-Al solid-liquid reaction milling,the powders product and their pureness were investigated by adding HCl,NaCl,KCl,Na_2SO_4 and stearic acid as process control agent.
研究HCl,NaCl,KCl,Na2SO4和硬脂酸等工艺过程控制剂(PCA)对Ni-Al固液反应球磨过程、粉末产量和粉末纯度的影响。
5) reactive ball-milling
反应球磨
1.
Mg base hydrogen storage material prepared by ball-milling and reactive ball-milling and its properties;
球磨和催化反应球磨制备的镁基复合贮氢材料及其性能
6) reactive ball milling
反应球磨
1.
This process is called reactive ball milling process (RBM).
本文综合评述了反应球磨(RBM)技术的原理、应用及其存在的问
2.
Reactive Ball Milling technology appeared after self-propagating phenomenon in the process of ball milling was discovered.
球磨过程中自蔓延现象的发现,促使了反应球磨技术(RBM)的产生。
3.
The hydrided Mg-3Ni-2MnO2 powder materials were prepared through the reactive ball milling under some hydrogen pressure,and its dehydrogenation kinetics properties were measured by the self-made apparatus too,further,the character of phase transformation behaviors was analyzed according to the Johnson-Mahl-Avrami equation.
利用充氢反应球磨技术制备了不同球磨时间的氢化态Mg-3Ni-2MnO2复合粉体材料,并对其放氢动力学性能进行了测试,进而利用J-M-A方程分析了放氢过程相转变行为特征。