1) sea ice bending failure
海冰弯曲断裂
2) bending fracture
弯曲断裂
1.
The bending fracture problems of cracked plate for anisotropic functionally graded materials under loads of pure bending,pure twisting or bending and twisting are discussed.
探讨各向异性功能梯度材料裂纹板受纯弯、纯扭、弯扭载荷作用下的弯曲断裂问题。
2.
The bending fracture problems of cracked plate for functionally graded materials under loads of pure bending,pure twisting or bending and twisting are discussed.
讨论功能梯度材料裂纹板受纯弯、纯扭、弯扭载荷作用下的弯曲断裂问题。
3) sea ice fracture
海冰断裂
4) flexure fracture force
弯曲断裂力
5) flexural fracture characteristic
弯曲断裂特征
6) bending fatigue fracture
弯曲疲劳断裂
1.
The results show that the break of gear belongs to bending fatigue fracture,the main bolt fracture bears from the root of gear teeth nearby transmission shaft,and the teeth break was caused by the bias load of the gear,the process was accelerated because of .
以上试验结果表明,轮齿为典型的弯曲疲劳断裂,裂纹起源于加载侧轮齿根部圆角表面处且靠近传动轴侧。
补充资料：弯曲工艺的概念及弯曲件
1．弯曲工艺：是根据零件形状的需要，通过模具和压力机把毛坯弯成一定角度，一定形状工件的冲压工艺方法。
2．弯曲成形工艺在工业生产中的应用：应用相当广泛，如汽车上很多履盖件，小汽车的柜架构件，摩托车上把柄，脚支架，单车上的支架构件，把柄，小的如门扣，夹子（铁夹）等。
弯曲的基本原理：以V形板料弯曲件的弯曲变形为例进行说明。其过程为：
1． 凸模运动接触板料（毛坯）由于凸,凹模不同的接触点力作用而产生弯矩， 在弯矩作用下发生弹性变形，产生弯曲。
2． 随着凸模继续下行，毛坯与凹模表面逐渐靠近接触，使弯曲半径及弯曲力臂均随之减少，毛坯与凹模接触点由凹模两肩移到凹模两斜面上。（塑变开始阶段）。
3．随着凸模的继续下行，毛坯两端接触凸模斜面开始弯曲。（回弯曲阶段）。
4．压平阶段，随着凸凹模间的间隙不断变小，板料在凸凹模间被压平。
5． 校正阶段，当行程终了，对板料进行校正，使其圆角直边与凸模全部贴合而成所需的形状。
弯曲变形的特点： 弯曲变形的特点是：板料在弯曲变形区内的曲率发生变化，即
弯 曲半径发生变化。从弯曲断面可划分为三个区：拉伸区、压缩区和中性层。