1) Short cut carbon felt
短切碳毡
2) Chopped carbon fiber mat
短切碳纤维毡
3) chopped strand mat
短切毡
1.
To prepare a fast wet-out,internally plasticizing binder for flexible E-glass fiber chopped strand mat,researches were made on both formulation and synthesizing technology.
从配方和工艺两方面着手,为制备出渗透快、内增塑的柔软性优良的无碱玻璃纤维短切毡粘结剂,研究了粘结剂配方中丙烯酸用量、自制内增塑单体配比、单体的加料顺序等对粘结剂性能的影响,而且考察了引发剂用量与反应温度的关系。
2.
This article introduces the equipment and technology for producing glass fiber chopped strand mat(CSM)by describing the key process parameters and main equipment units in the whole process, including the mat-forming section, binder section, oven section, wind-up section and line speed regulation.
叙述了短切毡生产流程中的成形段,粘结剂段,烘干段,卷取段以及生产线速度的调节所涉及到的主要工艺技术参数和主要设备及其工作原理。
3.
With ammonium persulfate/sodium thiosulfate as Redox initiator system,a binder based on vinyl acetate/acrylate copolymer used for chopped strand mat was prepared at low temperature.
以过硫酸铵/硫代硫酸钠为氧化还原引发体系,在低温下研究制备出了短切毡用的醋酸乙烯酯与丙烯酸酯类共聚物粘结剂。
4) chopped strand mat machine
短切毡机组
5) chopped random mat
短切无序毡
6) Chopped glass fiber mat
玻纤短切毡
补充资料：碳毡
分子式：
CAS号：
性质：碳纤维制成的毡，简称碳毡。以聚丙烯腈基碳毡为例，定积重量500g/m2和1000g/m2，纵向和横向强度(N/mm2)各为0.12，0.16和0.10，0.12，断裂伸长各为3％、4％和18％、16％，电阻率(Ω·mm)各为4～6，3.5～5.5和7～9，6～8，导热系数各为0.06W/(m·K)(25℃)，比表面积均>1.5m2/g，灰分皆小于0.3％，含硫量皆<0.03％。制法有：(1)碳短丝气流成网后针刺；(2)预氧丝毡碳化；(3)聚丙烯腈纤维毡预氧化和碳化。用作真空炉和惰性气体炉绝热材料、热的气体或液体和熔融金属滤材、燃料电池多孔电极、催化剂载体、耐腐蚀容器复合材料衬里和复合材料。
CAS号：
性质：碳纤维制成的毡，简称碳毡。以聚丙烯腈基碳毡为例，定积重量500g/m2和1000g/m2，纵向和横向强度(N/mm2)各为0.12，0.16和0.10，0.12，断裂伸长各为3％、4％和18％、16％，电阻率(Ω·mm)各为4～6，3.5～5.5和7～9，6～8，导热系数各为0.06W/(m·K)(25℃)，比表面积均>1.5m2/g，灰分皆小于0.3％，含硫量皆<0.03％。制法有：(1)碳短丝气流成网后针刺；(2)预氧丝毡碳化；(3)聚丙烯腈纤维毡预氧化和碳化。用作真空炉和惰性气体炉绝热材料、热的气体或液体和熔融金属滤材、燃料电池多孔电极、催化剂载体、耐腐蚀容器复合材料衬里和复合材料。