2) limit deep drawing height
极限拉深高度
1.
It is found that with the increase of radius of die and punch and deep drawing temperature,and the increase of friction coefficient between punch and blank, the limit deep drawing height increases,but with the increase of friction coefficient between binder and blank, and between.
研究得出:镁合金板料极限拉深高度在一定范围内随凸凹模圆角的增大、凸模与板料间摩擦因数的增大、温度的提高而增大,随凹模、压边圈与板料间摩擦因数的增大、拉深速度的提高而减小,而随压边力的增大先是增大后来减小,最佳压边力为7500N左右。
2.
Method of user subroutine and importing experimental stress-strain datas directly were used to get magnesium material model in ABAQUS respectively,the numerical simulation research of magnesium alloy limit deep drawing height was carried out at different temperatures.
结果表明:镁合金板料极限拉深高度在一定范围内随温度的提高而增大,本文提出的含非常软化因子的镁合金高温流变应力数学模型能较好地预测流变应力,通过二次子程序开发方法在ABAQUS软件中加入新的材料模型是切实可行的。
3) limit drawing height
极限拉深高度
1.
The results indicated the arrayed rule,density and diameter of the drawing holes affect the limit drawing height of sheet metal drastically.
分析结果表明,拉深孔排列规律、密度和孔径变化对板料的极限拉深高度有很大影响。
6) Limit depth
极限深度
1.
Rock burst s limit depth reduces with the ratio increase o.
分析了地下洞室围岩的应力状态 ,研究了岩爆极限深度问题 ,分析了应力路径的影响。
补充资料：极限拱顶高度试验
极限拱顶高度试验
limit dome height test
j ixian gongding gaodu shiyan极限拱顶高度试验(limit dome height test) 一种评估金属薄板成形性的试验方法，是杯突试验的改进。用以确定金属薄板在各种应变状态下的极限应变值。简称LDH试验。由于成形极限图的精度、重复性和稳定性较差，而一般的双向拉伸试验也只能提供等双向拉伸应变状态的试验参数，因此发展了极限拱顶高度试验。 试验方法类似于双向拉伸试验。工具有半球形凸模、凹模和带压边筋的压边圈。试验时，用球头凸模将金属板压入凹模。试样被压边圈压紧，以便使试样边缘的金属不能向凹模孔内流动。试验前在不同宽度的试样表面印制上网格。试验时在板料发生失稳或断裂的瞬间停机，并测量试徉的横向应变(短轴应变)。:和拱顶高度H，在以。:和H/凸模半径为横纵坐标轴的坐标系中标出不同宽度试样的试验点，把试验点相连即得图示的LDH曲线。LDH曲线与成形极限曲线形状相似，但要比制作成形极限曲线简便，并且在润滑条件相同的情况下，试验结果的重复性和稳定性都大大优于成形极限曲线。LDH曲线在坐标系中的位置越高，说明薄板在不同应变状态下的极限拉伸应变量越大，因此薄板的成形性能越好。 0 .74厂一一一一一一一门—~—一一一-门 0 .70卜一公幸、二乡」{ 哪。“L了场】卜洛」}/月 罗0 .66卜七‘暇.丫，1/} 升“’一{t少翅弓人{/} 旧}、{/1} 泛。62卜、}空_} o‘’8…圣翌eses二… 一10一5 0 5 10 E2 LDH曲线 (唐获)