1) Gd-Mn-Ti ternary system
Gd-Mn-Ti三元系
1.
The isothermal section of the phase diagram of the Gd-Mn-Ti ternary system at 773K has been investigated mainly by X-ray powder diffraction with the aid of differential thermal analysis and metallography.
本文用X射线衍射分析,差热分析等技术研究了Gd-Mn-Ti三元系合金相图773K等温截面。
2) Er-Mn-Ti ternary system
Er-Mn-Ti三元系
1.
The Phase relationship in the Er-Mn-Ti ternary system at 773K has been investigated by X-ray powder diffraction with the aid of differential thermal analysis(DTA)and optical microanalysis techniques in this work.
利用X射线衍射分析、差热分析以及金相分析等技术测定了Er-Mn-Ti三元系的相组成和相关系。
3) Au-Ag-Gd ternary systems
Au-Ag-Gd三元系
4) Gd-Ge-Sb ternary system
Gd-Ge-Sb三元系
1.
Phase relations in the Gd-Ge-Sb ternary system at 773K have beeninvestigated in this work.
本论文研究并确定了Gd-Ge-Sb三元系合金相图773k等温截面以及化合物CuSb_2Ti_5的晶体结构和热膨胀性能。
5) Gd-Co-Al ternary system
Gd-Co-Al 三元系
补充资料：三元系液化面投影图
三元系液化面投影图
projection of liquidus surface of ternary system
SCI rlyuanxI yehuamian tOuyIrigtLJ 三元系液化面投影图 (project’ion ofliqrlidus surIace o{ternary system) 将三元系统立体 相图中液化面上所有点、线、面以及具有一定温度间隔 的等温截面与液化面的交线等几何要素垂直投影到底 面等边三角形上的几何图形。通称三元相图。它是由三 角形的三条边、初晶区和等温线构成。通常还有分隔两 初晶区的界线(包括共熔线、转熔线和相变线等)、3个 初晶区的汇集点(包括三元共熔点、三元转熔点和三元 相变点)以及界线与边的交点(包括二元共熔点、二元 转熔点或二元相变点等)等结构要素；此外，在界线上 和边上用箭头表示温度的下降方向，，。并且以单箭头和 双箭头区分共熔曲线和转熔曲线。最简单的三元相图， 它由3个初晶区(A、B、c)、3条共熔线(EABEt、EAc Et、EBcEt)、1个三元共熔点(Et)、3个二元共熔点 (EAB、EBc、EAC)、3条边(AB、BC、AC)及若干条 等温线构成(见图)。 根据相律，三元凝聚系统中自由度数F、独立组元数C与相数P之间的关系可表示为 F—C—P+1—4一P可见，各初晶区是表示-种固相与液相平衡共存的单变量区，3个初晶区汇集点是3种固相与液相共存无变量点。在投影图上能够反映出三元系统中任一组成物质从完全熔化到完全固化的温度范围内的整个冷却进程，同时可利用杠杆法则计算冷却(或加热)过程中的固、液含量变化及固相组成变化。由于投影图是立体。相图的俯视图，因此，只能表示出液相面，对于液相面以下部分，如固相转变等就无法表示出来。为此，需要用一些等温截面，多温截面加以补充。 (张垂昌)