1) Nb-Ti-Co ternary system
Nb-Ti-Co三元系
1.
The isothermal section of Nb-Ti-Co ternary system rich in Co and Ti at 1173 K was determined by means of diffusion triple and electron microprobe analysis.
采用三元扩散偶技术测定了Nb-Ti-Co三元系富Co,Ti区域在1173K的等温截面,借助电子探针微区成分分析方法测定了Nb-Ti-Co三元扩散偶的相区成分,并对其相关系进行了研究。
2) Ti-Al-Nb ternary system
Ti-Al-Nb三元系
3) Nb-Ti-Si ternary system
Nb-Ti-Si三元系
1.
Phase equilibria in the Nb-Ti-Si ternary system at 1 473 K was investigated using diffusion triple technique and electron microprobe analysis (EMPA).
运用扩散偶技术结合电子探针微区成分分析方法对Nb-Ti-Si三元扩散偶进行相分析,测得Nb-Ti-Si三元系1473K下所生成的7个扩散层,分别是TiSi2,TiSi,Ti5Si4,Ti5Si3,Nb5Si3,NbSi2和M3Si,此扩散偶中未发现三元化合物。
4) Co Al Ti ternary system
Co-Al-Ti三元系
5) RE-Co-Ti ternary system
RE-Co-Ti三元合金系
6) Ti-Al-Nb ternary alloy
Ti-Al-Nb三元合金
1.
Referencing a lot of Ti-Al-Nb ternary phase diagrams and affection of alloy elements on binary Ti-Al phase diagram, a series of Ti-Al-Nb ternary alloy samples were produced by adjusting the contents of Nb and fixing the ratio of Ti and Al to 1.
本文参考了大量Ti-Al-Nb系各个温度下的三元相图,以及合金元素对二元Ti-Al相图的影响等文献,在Ti、Al等原子比的基础上,调整Nb的量设计并制备了一系列Ti-Al-Nb三元合金。
补充资料：Nb-Ti alloy
分子式：
CAS号：
性质：由金属铌和金属钛所组成的合金。工业生产的铌钛合金，钛含量一般为20%～60%（质量），最典型的铌钛合金含钛66%[约50%（质量）]。它们是重要的合金型超导材料，其超导转变温度为8～10K，加入其他元素还可以进一步提高超导性能。钛在合金中以固溶体状态存在。合金用混合粉末烧结和铌片、钛片组成的电极经真空自耗电弧炉或电子束熔炼数次成合金锭。
CAS号：
性质：由金属铌和金属钛所组成的合金。工业生产的铌钛合金，钛含量一般为20%～60%（质量），最典型的铌钛合金含钛66%[约50%（质量）]。它们是重要的合金型超导材料，其超导转变温度为8～10K，加入其他元素还可以进一步提高超导性能。钛在合金中以固溶体状态存在。合金用混合粉末烧结和铌片、钛片组成的电极经真空自耗电弧炉或电子束熔炼数次成合金锭。