1) Cu-Zr-Ti ternary alloy
Cu-Zr-Ti三元系
1.
By using CALPHAD technique, the driving forces for crystallization from the undercooled liquid in Cu-Zr-Ti ternary alloy were evaluated by means of Turnbull and Thompson-Spaepen (TS) Gibbs free energy approximate equations, respectively.
利用CALPHAD技术,分别采用Turnbull和Thompson-Spaepen(TS)两种近似公式计算了Cu-Zr-Ti三元系合金过冷熔体转变为晶体相的结晶驱动力。
2) Ti-Zr-Ni-Cu system
Ti-Zr-Ni-Cu系
1.
1474 nm has been designed in Ti-Zr-Ni-Cu system based on the quasicrystals-forming composition Ti40Zr40Ni20, then the alloy rods with diameter of 3 mm were fabricated by the conventional suction casting method.
以准晶成分Ti40Zr40Ni20为基准,在Ti-Zr-Ni-Cu系中设计出电子浓度为1。
3) Cu-Zr binary system
Cu-Zr二元系
4) Cu-Zr-Al ternary alloy
Cu-Zr-Al三元合金
5) Cu-Ti-Zr alloys
Cu-Ti-Zr合金
6) Cu-Zr-Ti alloys
Cu-Zr-Ti合金
补充资料：Mo-Ti-Zr-C alloy
分子式：
CAS号：
性质：由较高含量的钛、锆、碳与钼所组成的钼合金。最著名的称为TZC钼合金，含量为（%质量）钛1.25、锆0.15、碳0.15。该合金的硬度、高温强度比TZM钼合金高，但塑性较差，加工比较困难。钼钛锆碳合金可由熔炼成锭或粉末烧结成锭后加工制取各种型材，但要求较高的加工温度和加工压力。TZC钼合金主要以棒材、盘材用作金属高温热加工的模具，如粉末高温合金的等温锻造模具，有色及黑色金属的压铸模具、无缝钢管的穿孔顶头等。
CAS号：
性质：由较高含量的钛、锆、碳与钼所组成的钼合金。最著名的称为TZC钼合金，含量为（%质量）钛1.25、锆0.15、碳0.15。该合金的硬度、高温强度比TZM钼合金高，但塑性较差，加工比较困难。钼钛锆碳合金可由熔炼成锭或粉末烧结成锭后加工制取各种型材，但要求较高的加工温度和加工压力。TZC钼合金主要以棒材、盘材用作金属高温热加工的模具，如粉末高温合金的等温锻造模具，有色及黑色金属的压铸模具、无缝钢管的穿孔顶头等。