1) micro-grain
微米晶
2) submicron crystalline
亚微米晶
1.
Effects of annealing process on microstructure and properties of cold drawn submicron crystalline Cu-5wt%Cr alloy wires;
退火处理对冷拉拔亚微米晶Cu-5wt%Cr合金组织与性能的影响
2.
Through annealing and high temperature treatment,the recovery and recrystallization,the variations of microstructures and properties,and the thermal stability of submicron crystalline Cu-5%Cr wires after cold drawing have been investigated.
通过对冷拉拔的亚微米晶Cu-5%Cr丝材进行退火及高温热处理,研究其回复与再结晶、组织与性能的变化及其热稳定性。
3) micro-crystal bars
微米晶棒
1.
Synthesis of zinc phosphate micro-crystal bars by solid-phase chemical reaction at low temperature;
低热固相化学反应法合成磷酸锌微米晶棒
4) ZnO microcrystals
ZnO微米晶
1.
In this work, we have made systematical research on the hydrothermal synthesis, formation mechanism and optical properties of ZnO microcrystals in the presence of copper ion by virtue of comparability.
本论文比较了超声辅助和Cu~(2+)共存对100℃水热合成ZnO微米晶形貌的影响,结果表明:超声辅助和Cu~(2+)共存的协同作用合成了均一凸六棱柱状ZnO微米晶,而且这种形貌的ZnO具有很好的光致发光性能。
5) CuO microcrystals
CuO微米晶
6) microrod
微米晶体棒
参考词条
补充资料：多晶莫来石晶须(纤维)
分子式：
CAS号：
性质：莫来石相为主晶相的多晶纤维。化学成分为Al2O3 72％～77％，SiO222％～17％，B2O3 3％～5％，P2O51.5％～3.0％。纤维直径2～7μm，纤维长度20～125μm。使用温度1350℃。多采用溶胶-凝胶法制造。主要用作补强填料，也可作为轻质、隔热保温材料使用。
CAS号：
性质：莫来石相为主晶相的多晶纤维。化学成分为Al2O3 72％～77％，SiO222％～17％，B2O3 3％～5％，P2O51.5％～3.0％。纤维直径2～7μm，纤维长度20～125μm。使用温度1350℃。多采用溶胶-凝胶法制造。主要用作补强填料，也可作为轻质、隔热保温材料使用。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。