1) the mid-titanium slag
中钛型高炉渣
1.
The study of fired brick produced by the mid-titanium slag as the main raw material;
中钛型高炉渣制作烧结砖试验研究
2) slag containing high TiO 2
高钛型炉渣
3) medium-titania slag
中钛型炉渣
4) high Ti-bearing slag
高钛型高炉渣
1.
The preparation of slag brick could be a new method for optimizing compositions of the slag cementing material and the mathematical model is a useful tool to the material design for utilization of high Ti-bearing slag.
首次将支持向量机算法应用于优化胶凝材料的组成,建立了胶凝材料组成与28 d耐压强度的数学模型,并成功应用于实践,试制出高钛高炉渣掺量达80%以上的MU15矿渣实心砖,为攀钢高钛型高炉渣利用提供一条新的途径。
2.
Introduced Sichuan prestige group high Ti-bearing slag situation,and unifies high Ti-bearing slag the achievements in scientific research,proposed the Sichuan prestige group to high Ti-bearing slag synthesis recycling mentality and the forecast.
介绍了川威集团高钛型高炉渣的情况,并结合高钛型高炉渣的科研成果,提出了川威集团对高钛型高炉渣的综合回收利用的思路与展望。
5) high titaniferous blast-furnace slag
高钛型高炉矿渣
6) blast furnace slag bearing titania
高炉钛渣
1.
Analysis of carbothermal reduction of TiO_2 and extraction of titanium carbonitride from the blast furnace slag bearing titania;
TiO_2碳热还原与高炉钛渣提取碳氮化钛分析
补充资料：高炉渣的利用
高炉炼铁中由加入炉的矿石中的脉石、焦炭的灰分同熔剂反应熔化形成的副产物，是含有多种氧化物的复杂硅酸盐，常含有少量硫化物、氟化物和碳化物等。它的成分和产量因高炉原料和燃料的成分而有所不同。冶炼每吨铁生成的渣量（即渣铁比），大致为300～600公斤。高炉渣的主要成分为：CaO35～40％,SiO232～42％，Al2O36～16％，MgO4～13％,还含有少量MnO、FeO和S等。高炉渣的比重：液态2.2～2.5，固态2.3～2.7；出炉熔渣温度1400～1550℃，每公斤含热量400～460千卡。
熔融的高炉渣经缓冷、水淬和喷水等方法制成不同的建筑产品。
高炉渣的利用在美、日、法、英、联邦德国等国，基本上达到排渣和利用平衡，苏联1975年高炉渣的利用率达78.5％。中国目前每年约排出高炉渣2100万吨，约70％制成水渣，用作水泥原料，少量用作道碴和膨珠。
熔融的高炉渣经缓冷、水淬和喷水等方法制成不同的建筑产品。
高炉渣的利用在美、日、法、英、联邦德国等国，基本上达到排渣和利用平衡，苏联1975年高炉渣的利用率达78.5％。中国目前每年约排出高炉渣2100万吨，约70％制成水渣，用作水泥原料，少量用作道碴和膨珠。