1) high titanium-bearing slag
高钛高炉渣
1.
According to mineral characteristics and phase structure of high titanium-bearing slag,research progress on comprehensive utilization of the high titanium-bearing slag is reviewed.
从高钛高炉渣的特性和矿物相结构出发,回顾了高钛高炉渣综合利用的研究进展,提出高值利用高钛高炉渣的六个原则,指出高温碳化低温选择性氯化、等离子熔融还原提钛、冶金改性选择性析出分离是今后利用高钛高炉渣的方向。
2) blast furnace slag bearing titania
高炉钛渣
1.
Analysis of carbothermal reduction of TiO_2 and extraction of titanium carbonitride from the blast furnace slag bearing titania;
TiO_2碳热还原与高炉钛渣提取碳氮化钛分析
3) titanium-bearing blast furnace slag
含钛高炉渣
1.
Development of study on comprehensive utilization of titanium-bearing blast furnace slag;
含钛高炉渣综合利用研究的进展
2.
Synthesis of (Ca, Mg) α′-Sialon-AlN-TiN powders from titanium-bearing blast furnace slag;
含钛高炉渣合成(Ca,Mg)α′-Sialon-AlN-TiN粉末
3.
Preliminary study of synthesis compound fertilizer from titanium-bearing blast furnace slag
由含钛高炉渣合成复合肥初探
4) Ti-bearing blast furnace slag
含钛高炉渣
1.
Green separation technique of Ti component from Ti-bearing blast furnace slag;
含钛高炉渣中钛组分的绿色分离技术
2.
The significance and present research state of comprehensively utilizing Ti-bearing blast furnace slag are overviewed.
对含钛高炉渣综合利用意义、研究现状进行了概述,分析了含钛高炉渣利用过程中存在的主要问题。
3.
Modifying the phase structure of Ti-bearing blast furnace slag by using physical chemistry method is the key to utilization of Ti-bearing blast furnace slag;Back scattered image,X-ray energy spectrum analysis and X-ray diffraction analysis of the raw slag and modified slag were carried out.
改变含钛高炉渣中矿相组成的研究是含钛高炉渣综合利用的关键;通过背散射电子形貌像、X射线能谱分析和X射线物相分析等手段,对氧化前的含钛高炉渣及其氧化改性后的渣样进行分析,表明氧化后渣中含钛相的形貌、成分和相结构等发生变化;钛的赋存状态也发生相应的改变。
5) slag containing vanadium and titanium
钒钛高炉渣
1.
Study on the determination of metal iron in slag containing vanadium and titanium by iodine-alcohol dissolution;
碘-乙醇分离钒钛高炉渣中金属铁的研究
6) Rich titanium blast furnace slag
富钛高炉渣
补充资料:高炉泡沫渣
高炉泡沫渣
the foaming slag of blast furnace
一定值后会有大量气体以气泡形式分散于渣中使炉渣的体积膨胀‘这种炉渣即为泡沫渣,它是特殊矿冶炼高炉造渣的一个重要问题。泡沫渣的产生将造成高炉生产过程渣铁出不尽,料柱透气性恶化,风口易挂渣,给高炉炉况顺行和强化带来困难。当炉渣进入渣罐后由于其体积膨大使渣罐利用率降低,甚至从渣罐上部溢出,造成事故。泡沫渣的形成有两个条件,一是有大量的分散气体生成,二是炉渣性能使分散气体稳定存在,从而使渣中气体量不断增加。在钒铁磁铁矿的高炉冶炼中,高炉下部有较多的Feo、TIO:等氧化物从渣中还原,从而产生大量CO气体。同时,高钦型高炉渣表面吸附,富集的活性物质比普通渣高得多。表面活性物.的存在使液膜的表面私度比体积豁度高,从而阻碍了排气速度,延长了泡沫的寿命。表面活性物的存在又使炉渣表面张力大大下降,造成渣内分散气泡合并上浮困难,使气泡更稳定,从而形成泡沫渣。解决泡沫渣间题的办法是采用一切手段提高渣中“氧势”,抑制TIOZ还原,减少Ti(C、N)等胶质微粒的生成,也即减少表面吸附的活性物质量,从而阻止泡沫形成。goolu Paomozha高炉泡沫渣(the foaming、lag。f blast fur-nace)高炉冶炼钒钦磁铁矿时,炉渣中Tio。高达
说明:补充资料仅用于学习参考,请勿用于其它任何用途。