1) Pr-ion defects
Pr离子缺陷
1.
The calculated activation energies U(H) of flux motion increased drasticallyin the samples with proper amount ofPr-ion defects.
Pr部分替代Ca可以在Bi-2223的超导层中引起局域缺陷(简称Pr离子缺陷),本文分析了不同含Pr量的Bi-2223/Ag带材在垂直于带面的外场下电阻转变特性,研究了其磁通钉扎势垒的变化规律。
2) Ionic defect
离子缺陷
3) anion defact
阴离子缺陷
4) ion beam defect engineering
离子束缺陷工程
5) defect factor
缺陷因子
6) defective particles
缺陷粒子
1.
For searching the burst cause of PVC-U pipes during hydrolic test under low pressure, the cracked sections of those PVC-U pipes were observed and the defective particles were found in them.
为探索在试压时低压下即破裂的硬聚氯乙烯 (PVC U)管材的破裂原因 ,对这些破裂管材的断裂面进行了仔细观察 ,发现在这些断裂面上均有缺陷粒子存在。
补充资料：点缺陷(见晶体缺陷)
点缺陷(见晶体缺陷)
point defect
点缺陷point defeet见晶体缺陷。