1) Ti-Cr multi-layer film
钛-铬多层膜
2) lead-zirconate titanate multilayer film
锆钛酸铅多层膜
3) porous Ti membrane
多孔钛膜
4) TiN/AlN nano-multilayer films
氮化钛/氮化铝纳米多层膜
1.
TiN/AlN nano-multilayer films were prepared on single crystal silicon wafer and high-speed steel using a new sputtering setup designed and manufactured based on high-rate reactive magnetron sputtering.
采用新型高速反应真空磁控溅射系统制备了氮化钛/氮化铝纳米多层膜,探讨了周期(λ)对多层膜力学性能及抗磨性能的影响;在微钻针及车刀表面分别制备了上述多层膜,并分别对电路板以及中碳钢棒进行实机加工测试,以验证其实用性。
5) TiO2/porous Ti composite membrane
二氧化钛/多孔钛复合膜
1.
The results showed that the TiO2/porous Ti composite membranes,which were dip-coated more than three times,could be inhibited the passage of immunoglobulin and immune cells.
实验结果显示,所制得的二氧化钛/多孔钛复合膜经过3次以上涂膜能有效地阻隔免疫球蛋白及免疫细胞,但小分子物质(如葡萄糖)能自由通过该膜,故该复合膜可以作为免疫隔离膜使用,并且具有良好的免疫隔离效果。
6) ordered porous TiO2 film
二氧化钛多孔膜
1.
Three-dimensionally ordered porous TiO2 films were prepared by sol-dipping method using silica spheres multilayer templates.
以该阵列为模板,通过在TiO_2前驱体溶胶中多次浸渍热处理循环,随后采用超声辅助的NaOH溶液腐蚀去除硅球模板,制备了>20层厚的反转结构的二氧化钛多孔膜。
补充资料：全氟羧酸-磺酸多层阳离子交换膜
分子式：
CAS号：
性质：又称全氟羧酸-磺酸多层阳离子交换膜，需在膜的一面形成一羧酸膜层。其制法是将全氟磺酸膜片与全氟羧酸膜片加热层压而成，或在全氟磺酸膜的一面经化学处理，使—SO3H转换成—COOH基。这种离子膜一面为—SO3H基，另一面为—COOH，用聚四氟乙烯织物增强，在氯化钠电解制碱中的电流效率为95%左右。
CAS号：
性质：又称全氟羧酸-磺酸多层阳离子交换膜，需在膜的一面形成一羧酸膜层。其制法是将全氟磺酸膜片与全氟羧酸膜片加热层压而成，或在全氟磺酸膜的一面经化学处理，使—SO3H转换成—COOH基。这种离子膜一面为—SO3H基，另一面为—COOH，用聚四氟乙烯织物增强，在氯化钠电解制碱中的电流效率为95%左右。