1) large-strain rolling
大应变轧制
2) plain strain rolling
平面应变轧制
3) rolling deformation
轧制变形
1.
The influence of rolling deformation and heat treatment temperature on structures, mechanical properties is studied.
X射线衍射结果表明,随着轧制变形量的增加,Ti50Ni47Fe3合金在轧制方向上出现了择优取向;Ti50Ni47Fe3合金的晶粒尺寸随着轧制变形量的增加而减小,随着热处理温度的升高而增大;Ti50Ni47Fe3合金的抗拉强度和屈服强度随着轧制变形量的增加而增大,随热处理温度的升高而降低。
2.
The results show that the orientation distribution calculated by the FC (full constraints)Taylor model is closer to experimental results than those by other models at the low rolling deformation de.
结果表明:在低轧制变形程度时,完全限制(FC)模型计算结果的取向分布较其它模型更符合实际结果。
3.
The results show that the rolling textures for the sample with initial randomly distributed texture mainly consists of C,S and B components during rolling deformation while the orientation density values for the three textures only have slight difference, most crystallites a.
结果表明:随着轧制变形的进行,对于初始自由分布的样品,晶粒取向主要向α,β取向线附近聚集,其形变织构主要由C,S及B织构组成,且3种织构成分密度值相差不大;对于初始具有近似立方织构的样品,晶粒取向主要向β取向线上聚集,其形变织构主要由C,S织构组成,B织构成分相对较弱。
4) rheorolling
流变轧制
1.
Microstructural characteristics of electromagnetically stirred semi-solid 60Si2Mn steel after rheorolling;
电磁搅拌的半固态60Si2 Mn钢流变轧制的组织特征
2.
High carbon tool steels processed by conventional processing methods and semi-solid rheorolling technology are discussed.
探讨了高碳工具钢常规的加工方法和半固态流变轧制技术,结果表明将在凝固过程中进行搅拌后制备的高碳工具钢半固态浆料直接进行流变轧制,可生产出成分均匀、没有偏析的产品,消除了在常规轧制中很难克服的网状碳化物等缺陷;半固态固相颗粒细小而且星球状可生产出高强、高韧性的工具钢。
5) Thixorolling
触变轧制
6) thermomechanical rolling
形变轧制
补充资料：轧制
冶金厂最主要的金属塑性加工方法。金属通过旋转的轧辊产生塑性变形。轧制可按轧辊和轧件的相互位置、运动和延伸的方向分为纵轧、横轧和斜轧。轧制也可按金属在轧制时是否立即产生软化（回复和再结晶分为热轧和冷轧。一般把金属在再结晶温度以上的轧制称作热轧,把有加工硬化的轧制称作冷轧。此外,轧制还可按轧制品种分类，如板带材轧制、管材轧制、型材轧制、线材轧制和周期断面轧制等。也有按轧制阶段分为粗轧和精轧的。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。