1) cold heading forming
冷镦成形
2) upsetting-extrusion forming
镦挤成形
1.
Numerical simulation of restrained split-flow in upsetting-extrusion forming of cylinder gear;
圆柱齿轮镦挤成形约束分流的数值模拟
3) upsetting process
镦粗成形
1.
Coupled thermo-mechanical FEM analysis of the sintered powder during upsetting process;
粉末烧结体镦粗成形过程热力耦合有限元分析
4) electric upsetting
电镦成形
1.
Research on some key techniques of coupled thermo-mechanical FEM simulation for electric upsetting process;
电镦成形过程电热力耦合有限元模拟若干关键技术的处理
5) heat forming
热镦成形
1.
Regarding heat forming process of 1Cr18Ni9Ti as typical forging process, this paper studied the law of various technological parameters on 1Cr18Ni9Ti by means of Gleeble-1500 Thermo-simulation machine and metal-scope.
以 1Cr18Ni9Ti奥氏体不锈钢热镦粗锻造工艺为例 ,通过Gleeble— 150 0热模拟试验机和金相显微镜等手段 ,研究了工艺参数对 1Cr18Ni9Ti热镦成形的影响 ,结果表明 :温度、应变速率、变形程度对热镦成形过程的流动应力和变形后试件的晶粒大小、硬度具有明显的影响规律 ,对于控制奥氏体不锈钢的锻造性能具有重要的指导意
6) forming in final heading
终镦成形
补充资料：自动冷镦机、多工位螺栓自动冷镦机
| |||||||
主要参数内容 | 国际先进 | 国内先进 | 国内一般 | 国内落后 | 评定方法及说明 | ||
（一）加工精度 | 参照GB9166-88、JB/T3053-91 | ||||||
1、冲头夹持器模孔中心线对夹持器后支承面的垂直度（mm） 在100长度上 | 0.008 | 0.01 | 0.015 | ＞0.015 | |||
2、凹模座模孔中心线对凹模后座支承面的垂直度（mm） 在100长度上 | 0.008 | 0.01 | 0.015 | ＞0.015 | |||
3、冲头夹持器模孔中心线对滑块行程的平行度（mm） 在100行程上 | 0.016 | 0.02 | 0.02 | ＞0.02 | |||
4、滑块行程对机身上与凹模座贴合的垂直面的垂直度（mm） 在100行程上 | 0.016 | 0.02 | 0.02 | ＞0.02 | |||
5、工件头部对工件杆部中心线的偏移量（mm） | ＜0.20 | 0.20~0.25 | 0.25~0.30 | ＞0.30 | |||
（二）生产率（件/分） | |||||||
20mm | ＞80 | 70 | 65 | ＜65 | |||
30mm | ＞60 | 50 | 45 | ＜45 | |||
说明：补充资料仅用于学习参考，请勿用于其它任何用途。