1) inorganic zinc-rich
无机富锌
1.
The curing mechanism of inorganic zinc-rich painting is very special and the application must be carried out very carefully especially the thickness of film and the environmental humidity must be in the correct scope.
无机富锌涂料是海洋平台涂装中经常使用的一种底漆,它不但具有优良的防腐蚀性能,同时也能够形成对基体钢材的阴极保护。
2) inorganic zinc rich coating
无机富锌漆
1.
In this article, we have discussed the category, property and application of aqueous inorganic zinc rich coating at home nowadays.
讨论了目前国内水性无机富锌漆的种类、性能和应用 ,比较了几种代表性的水性无机富锌漆及其优点 ,探索了无机富锌漆的性能改进 ,从环保角度出发 ,水性无机富锌漆具有良好的开发前
3) inorganic zinc-rich coatings
无机富锌涂料
1.
Through application of frankincense resin in epoxy coatings,inorganic zinc-rich coatings and acrylic coatings.
分析了乳香树脂的结构和性能,通过其在环氧涂料、无机富锌涂料和丙烯酸涂料的应用研究,发现乳香树脂能够提高涂料的机械性能和耐腐蚀性能。
2.
In view of environmental protection, water-borne inorganic zinc-rich coatings, especially for whose binder used is potassium silicate solutions, become one of the most hopeful categories available today in the field of heavy-duty anticorrosion, for its cheap cost and outstanding performance.
随着人们环保意识的逐渐增强,水性无机富锌涂料,尤其是以硅酸钾水溶液为基料的富锌涂料,以其廉价的成本和优异的性能已成为环保型重防腐涂料中最重要的品种之一。
4) inorganic flake zinc-rich
片状无机富锌
1.
sol, alkoxy silane and water as raw material, in a certain temperature range through orthogonal experimental, synthesis of a high modulus potassium silicate solutions as inorganic flake zinc-rich coating with the base material.
本文通过对硅酸钾、硅溶胶、烷氧基硅烷性能的研究，反应温度的影响，确定了以硅酸钾、硅溶胶、烷氧基硅烷及水为原料，在一定温度范围内通过正交实验合成了高模数硅酸钾溶液作为片状无机富锌涂料用基料，与适量锌粉混合后配制成片状无机富锌涂料。
补充资料：无机富锌车间底漆
分子式：
CAS号：
性质：此类涂料主要由基料、锌粉、着色颜料、填充料和添加剂等组成。基料起黏结锌粉的作用，主要品种有硅酸烷基酯、硅酸烷基酯/钛酸烷基酯、硅酸烷基酯/硼酸烷基酯及其他改性品种。锌粉一般用超细锌粉，颗粒度0.2～12μm，平均粒度5μm，用量50％～80％。施工干膜厚一般20μm左右，兼具电化学保护和化学防蚀双重作用。户外耐久性可达6～8个月，适用于周期较长、防腐蚀要求较高的场合(如造船业防腐)。
CAS号：
性质：此类涂料主要由基料、锌粉、着色颜料、填充料和添加剂等组成。基料起黏结锌粉的作用，主要品种有硅酸烷基酯、硅酸烷基酯/钛酸烷基酯、硅酸烷基酯/硼酸烷基酯及其他改性品种。锌粉一般用超细锌粉，颗粒度0.2～12μm，平均粒度5μm，用量50％～80％。施工干膜厚一般20μm左右，兼具电化学保护和化学防蚀双重作用。户外耐久性可达6～8个月，适用于周期较长、防腐蚀要求较高的场合(如造船业防腐)。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条